The paper presents experimental verification of customized resistive crack propagation sensors as an alternative method for other common structural health monitoring (SHM) techniques. Most of these are sensitive to changes in the sensor network configuration and a baseline dataset must be collected for the analysis of the structure condition. Sensors investigated within the paper are manufactured by the direct-write process with electrically conductive, silver-microparticle-filled paint to prepare a tailored measuring grid on an epoxy or polyurethane coating as a driving/insulating layer. This method is designed to enhance the functionality and usability compared to commercially available crack gauges. By using paint with conductive metal particles, the shape of the sensor measuring grid can be more easily adapted to the structure, while, in the previous approach, only a few grid-fixed sensors are available. A fatigue test on the compact tension (CT) specimen is presented and discussed to evaluate the ability of the developed sensors to detect and monitor fatigue cracks. Additionally, the ARIMA time series algorithm is developed both for monitoring and predicting crack growth, based on the acquired data. The proposed sensors’ verification reveal their good performance to detect and monitor fatigue fractures with a relatively low measurement error and ARIMA estimated crack length compared with the crack opening displacement (COD) gauge.

This paper presents the results of investigations of the effect of graphene oxide and surface shot peening on the mechanical properties and fatigue life of bolts made of austenitic 304 steel. An innovative method for the uniform deposition of graphene oxide on screws is presented. The process involved activating the surface using plasma and then performing graphene oxide deposition using centrifugal force and vacuum drying. The screw specimens prepared in this way were subjected to a surface peening process. Comparative studies have shown that the combination of graphene oxide deposition and shot peening processes results in an increase in fatigue life of approximately 42 ÷ 275% (depending on the stress amplitude level) compared to the as-delivered samples. The results presented are promising and may provide a basis for further research on the application of graphene and its derivatives to increase fatigue life and improve the mechanical properties of machine components.

Military aircraft are subjected to highly variable and unpredictable loads due to diverse mission profiles, armament configurations, and individual piloting styles. This variability complicates the definition of precise load spectra, particularly in cases where data loss occurs due to Flight Data Recorder (FDR) malfunctions or data mishandling. This paper investigates the use of different flight parameters, such as load factor ( n _z ), barometric height ( H _b ), and horizontal velocity ( V _p ), to define load sequences for the PZL-130 “Orlik” TC-II military trainer aircraft. These sequences were then used to evaluate crack propagation using Compact Tension (CT) specimens. The results show that the incorporation of additional flight parameters improves the accuracy of crack propagation predictions when compared to direct strain measurements. This study highlights the potential of using available flight data to develop reliable load spectra for fatigue life estimation in military aircraft, even when direct load measurements are not financially feasible.

The objective of the research presented in this paper was to determine the honeycomb core compliance of a sandwich structure of the horizontal stabilizer of the MiG-29 fighter jet in the static compression test. The study of the specimen was conducted based on the ASTM C365/C365M standard. The article presents the results of experimentally determined dependencies and strength parameters, i.e. the force-displacement dependence, the compressive modulus and the honeycomb core deformations.

In this work, the compressive residual strength tests results, Compression After Impact (CAI), are presented. The specimens were made of carbon-epoxy prepreg E722-02 UHS 130-14. Two variants of specimens were tested: samples undamaged and samples with damage that was centrally introduced by a drop-weight impact, as per the ASTM D7136/7136M standard. An impactor with potential energy equal to 15J and the type of support required by the standard were used. The size of impacted damages, defined as an area of damage on a plane perpendicular to the impact direction, and the equivalent diameter were specified using the flash thermography method. The tests were performed using the fixtures manufactured according to the ASTM D7137/7137M standard. The specimens were compressed to determine the residual strength. This value was afterwards used to specify the force levels for the fatigue tests. The fatigue tests were carried out under force control – with a sinusoidal shape, stress ratio R equal to 0.1 and frequency f 1Hz. Maximum force in a loading cycle P _max was being increased after each thousand of cycles N until its value was close to the residual strength determined in the previously mentioned tests. In this work, the following relationships were presented: force - displacement P- δ for both static and fatigue tests and displacement-loading cycles δ- N for fatigue tests. A method of conducting the fatigue tests of CFRP composite was proposed, in which both the CAI specimens and CAI fixture were used. This allowed researchers to accelerate making initial comparisons between the two groups of specimens with damages – grouped relative to the way of conditioning.

Laboratory for Materials Strength Testing (LMST) has been conducting accredited mechanical research for aviation from 2003. Among accredited procedures are e.g. low and high cycle fatigue tests, fracture toughness tests and fatigue crack growth rate tests. The main goal of them is obtaining materials constants and characteristics. However knowledge how to conduct these tests could be used also in other applications, for instance in the work on development of Structural Health Monitoring systems (SHM). When cracks propagate in a controlled way in laboratory conditions, it allows verifying the operation of a single sensor or a network of sensors. In this paper, an overview of mechanical tests carried out at the Laboratory for Materials Strength Testing within Air Force Institute of Technology (AFIT) work on research and development of SHM systems is presented. Specimens prepared from materials such as aluminum alloys (among other withdrawn PZL-130 Orlik TC-II aircraft) and CFRP composite were tested under different mechanical loads, i.e., cycle and impact loads. In the presented research, both constant amplitude and spectrum loads were applied.