In this paper, we present an approach to fatigue estimation of a Main Landing Gear (MLG) attachment frame due to vertical landing forces based on Operational Loads Monitoring (OLM) system records. In particular, the impact of different phases of landing and on ground operations and fatigue wear of the MLG frame is analyzed. The main functionality of the developed OLM system is the individual assessment of fatigue of the main landing gear node structure for Su-22UM3K aircraft due to standard and Touch-And-Go (T&G) landings. Furthermore, the system allows for assessment of stress cumulation in the main landing gear node structure during touchdown and allows for detection of hard landings. Determination of selected stages of flight, classification of different types of load cycles of the structure recorded by strain gauge sensors during standard full stop landings and taxiing are also implemented in the developed system. Based on those capabilities, it is possible to monitor and compare equivalents of landing fatigue wear between airplanes and landing fatigue wear across all flights of a given airplane, which can be incorporated into fleet management paradigms for the purpose of optimal maintenance of aircraft. In this article, a detailed description of the system and algorithms used for landing gear node fatigue assessment is provided, and the results obtained during the 3-year period of system operation for the fleet of six aircraft are delivered and discussed.

The Polish Air Force operates more than one hundred helicopters of the Mi family (manufactured by Mil Helicopters), equipped with metal main rotor blades. The main rotor blades are among the most stressed components of these structures. For this reason, they are subject to more frequent inspections during operation than other components. One type of damage detected during inspections is the local disbonding of fragments of the anti-erosion layer from the leading edge. This harmless-looking damage is very dangerous, since it quickly leads to the complete detachment of the layer. The leading edge, unprotected by the metal cover, erodes rapidly. The detached layer, when thrown away at high speed, endangers other parts of the helicopter, such as the tail rotor, and may cause damage to other helicopters if flying in formation. The technology supplied by the manufacturer to date has not encompassed the field repair of this type of damage. Therefore, efforts were made to develop repair technology for rapid repairs of blades in field conditions during missions of the Task Force White Eagle in Afghanistan. This article presents the concept of repair technology feasible in field conditions and presents the results of post-repair edge tests. Test results to identify the materials used in the construction of the trailing edge are also presented. The results of materials testing facilitated the development of technological processes, and, in the future, will aid the selection of a substitute bonding paste system with similar parameters that are essential for repairs.

Military aircraft are subjected to variable loads, which are the main cause of initiation and propagation of cracks in the most stressed locations of the airframe. The aim of a Full-Scale Fatigue Test (FSFT) is to represent actual load conditions in such a way that the results obtained are a good representation of the actual loads and may be used as data that give insight into the development of real fatigue damage in critical locations. The FSFT load spectrum is a generalized depiction of the expected service loads and is designed to give an overall good representation of loads exerted on the airframe’s structural elements during operation. Moreover, the discrete method of load application on the structure (exerting loads with hydraulic actuators rather than pressure fields or inertia loads expected in actual operation) may cause some local effects, which may not be present in operation. The proposed usage of direct strain data from the test include such local effects. Moreover, operational loads may vary between individual aircraft, therefore it is crucial to understand the whole process of fatigue crack onset and development in order to determine safe inspection intervals and thereby mitigate risk. This paper presents crack propagation calculations regarding the development of a crack in a critical location of the PZL-130 “Orlik” TC-II aircraft, discovered during FSFT. The discussed crack was found already developed, hence the information about nucleation and initial propagation of the crack was not available. Therefore, there was a need to recreate the whole propagation process by means of numerical estimations using the FSFT results like location of the crack and total life for model validation. Moreover, in order to gather real load data for calculations a dedicated stain gage was installed on the damaged load path to monitor the actual remote strain in the element during the FSFT. This allowed for the definition of load sequence exerted on the damaged element directly during the test rather than estimating it from the general load conditions of the wing. The calculations allowed for the estimation of crack propagation curves from initiation to critical crack length causing fatal damage. The obtained curves allowed to visualize the crack behavior due to applied load and furthermore define initial and recurring inspection intervals for the entire fleet during operation, which allowed to define which cracks could be found before they reach critical size in order to carry out mitigation actions like repair or replacement of the damaged part. The authors present the methodology for load spectrum development based on direct strain measurements and furthermore crack propagation curves estimation, validated with the actual FSFT results, which allowed to propose nondestructive inspection intervals for future operation.

The following paper aims to provide the results of an innovative structural crack detection technique using printed adaptive sensors. They were manufactured using conductive ink with silver microparticles and polymer insulators. The technique leveraged the unique properties of Direct Ink Write additive manufacturing combined with domain knowledge in the field of technical condition monitoring. The goal was to achieve high sensitivity and precision in detecting fatigue-crack-induced changes in structural components. The sensors’ fabrication repeatability, output stability, and crack detection capabilities were investigated. Based on preliminary measurements of the sensors’ output characteristics, the analyzed data showed that a tolerance in the range of 5% can be obtained for batch production. Damage size estimation using this new crack gauge during a fatigue crack growth test was high compared to the reference, with less than 1 mm precision over 30 mm of crack length. Throughout the fatigue test of up to 1.5 million cycles, all CCPSs remained fully functional, with no failure-related changes in their output signal patterns. The proposed sensor has proven its reliability for the detection of fatigue cracks and propagation monitoring and is a good alternative to other SHM technologies for this purpose.

Thermoplastic composites are growing in popularity in the aerospace and automotive industries; they enable weldable and recyclable structures. Resistance welded hybrid thermoplastic and metal joints are attractive for rapid assembly, but the thermal mismatch between metals and polymers introduces residual stresses, which can drive edge debonding and compromise durability. This study presents fabricated single-lap PC/CF–Al7075 coupons with measured mid-span bow resulting from welding, evaluated bond quality by step-heating thermography, and an evaluated framework for residual stress prediction using Ansys complemented by a bimetal analytical check. Three thermal cycles were examined with different temperature gradients (200, 220, 240 °C): the measured bow was 16.5 mm and remained constant, whereas analytical calculation increased with ΔT similarly to the FEM prediction. The current FEM under predicted the bow (Mean Absolute Percentage Error is 21%), showing stress contours that decay with distance from the bond and revealing pronounced peaks in both σ_xx and σ_zz components at weld edges, consistent with shear-lag theory. FEM returned edge-peaked peel rising from 43 to −64 MPa and σ_xx was up to 12% more compressive than analytical calculation; an effective CF/PC CTE of 1.5 × 10⁻⁶ K⁻¹ reconciled curvature with test better than catalogue values. The temperature insensitive bow is attributed to polycarbonate flow/viscoelastic relaxation above Tg and hot relaxation in aluminum, with effects not represented in the elastic models. Edge peel and shear govern initiation risk.