We address the behavior in which a bias voltage can be used to switch on and off the photoluminescence of a planar film of methylammonium lead triiodide perovskite (MAPbI₃) semiconductor with lateral symmetric electrodes. It is observed that a dark region advances from the positive electrode at a slow velocity of order of 10 μm s^–1. Here we explain the existence of the sharp front by a drift of ionic vacancies limited by local saturation, that induce defects and drastically reduce the radiative recombination rate in the film. The model accounts for the time dependence of electrical current due to the ion-induced doping modification, that changes local electron and hole concentration with the drift of vacancies. The analysis of current dependence on time leads to a direct determination of the diffusion coefficient of iodine vacancies and provides detailed information of ionic effects over the electrooptical properties of hybrid perovskite materials.

The power conversion efficiency of inorganic–organic hybrid lead halide perovskite solar cells (PSCs) is approaching that of those made from single crystalline silicon; however, they still experience problems such as hysteresis and photo/electrical‐field‐induced degradation. Evidences consistently show that ionic migration is critical for these detrimental behaviors, but direct in‐situ studies are still lacking to elucidate the respective kinetics. Three different PSCs incorporating phenyl‐C61‐butyric acid methyl ester (PCBM) and a polymerized form (PPCBM) is fabricated to clarify the function of fullerenes towards ionic migration in perovskites: 1) single perovskite layer, 2) perovskite/PCBM bilayer, 3) perovskite/PPCBM bilayer, where the fullerene molecules are covalently linked to a polymer backbone impeding fullerene inter‐diffusion. By employing wide‐field photoluminescence imaging microscopy, the migration of iodine ions/vacancies under an external electrical field is studied. The polymerized PPCBM layer barely suppresses ionic migration, whereas PCBM readily does. Temperature‐dependent chronoamperometric measurements demonstrate the reduction of activation energy with the aid of PCBM and X‐ray photoemission spectroscopy (XPS) measurements show that PCBM molecules are viable to diffuse into the perovskite layer and passivate iodine related defects. This passivation significantly reduces iodine ions/vacancies, leading to a reduction of built‐in field modulation and interfacial barriers.

Charge carriers’ density, their lifetime, mobility, and the existence of trap states are strongly affected by the microscopic morphologies of perovskite films, and have a direct influence on the photovoltaic performance. Here, we report on micro-wrinkled perovskite layers to enhance photocarrier transport performances. By utilizing temperature-dependent miscibility of dimethyl sulfoxide with diethyl ether, the geometry of the microscopic wrinkles of the perovskite films are controlled. Wrinkling is pronounced as temperature of diethyl ether (T_DE) decreases due to the compressive stress relaxation of the thin rigid film-capped viscoelastic layer. Time-correlated single-photon counting reveals longer carrier lifetime at the hill sites than at the valley sites. The wrinkled morphology formed at T_DE = 5 °C shows higher power conversion efficiency (PCE) and better stability than the flat one formed at T_DE = 30 °C. Interfacial and additive engineering improve further PCE to 23.02%. This study provides important insight into correlation between lattice strain and carrier properties in perovskite photovoltaics.