In the field of metallurgy, there are many factors that influence the final quality of cast iron. These are mainly charge materials, chemical composition and metallurgical preparation up to the final casting process. Even small deviations from metallurgical processing lead to fluctuations in melt quality and the occurrence of casting defects. Charge materials have a significant impact on the quality of cast iron, especially steel scrap, which is increasingly used from an economic and ecological point of view, especially when melting cast iron in electric furnaces. Cast iron produced from a higher proportion of steel scrap in the charge has a higher hardness and tensile strength. On the other side, these cast irons have a higher tendency of chillout, brittleness, shrinkage, pearlitic microstructure, stresses and higher purity due to the difference in hardness at different wall thicknesses of the castings. It is the high hardness that is the problem in the final machining of castings. These negative properties are recorded mainly in heavy thick-walled castings with a higher tensile strength and hardness. This negative effect is mainly due to the nitrogen content in the steel scrap. Based on this knowledge, operating melts were realized in the foundry’s operating conditions. The influence of steel scrap in the charge and the possibility of eliminating its negative effects on the properties of cast iron were investigated.

The production of high-quality castings without foundry defects at minimal production costs is a constant priority for foundries. Innovation and optimization of production processes are key to achieving this goal. Computer simulation of foundry processes offers a modern alternative to expensive and time-consuming experiments in real foundries and provides a reliable representation and analysis of casting and solidification processes. A detailed analysis of the casting and solidification simulation results allows the prediction of various risks that can cause defects in cast castings, thereby reducing their quality and, last but not least, the cost of their production. This paper deals with the analysis of a computer simulation of the casting of a brake disc in a Slovak foundry. This brake disc has had shrinkages and micro shrinkages that reduce the internal quality of the casting. These defects occurred in the ribs in the upper part of the casting under the feeders. A computer simulation of the casting and solidification of this casting was made according to the real conditions. It turned out that the designed gating system with a system of feeders was not sufficient to eliminate the emerging defects. A new layout for the feeders was proposed, which ultimately eliminated the occurrence of defects based on the results of the computer simulation. The input parameters were set to be as close as possible to the actual needs of the foundry. Moreover, 3D models of the assemblies were designed in SolidWorks Premium 2015 x64 Edition CAD software, and the filling and solidification simulations were performed using the NovaFlow & Solid CV 4.6r42 simulation program.

In the field of metallurgy, there are many factors that influence the final quality of cast iron. These are mainly charge materials, chemical composition, metallurgical preparation up to the final casting process. Even small deviations from metallurgical processing lead to fluctuations in melt quality and the occurrence of casting defects. Charge materials has a significant impact on the quality of cast iron, especially steel scrap, which is increasingly used from an economic and ecological point of view, especially when melting cast iron in electric furnaces. Cast iron produced from a higher proportion of steel scrap in the charge has higher hardness and tensile strength. On the other side, these cast irons has a higher tendency to chillout, brittleness, shrinkage, pearlitic microstructure, stresses and higher purity due to the difference in hardness at different wall thicknesses of the castings. It is the high hardness that is the problem in the final machining of castings. These negative properties are recorded mainly in heavy thick-walled castings with higher tensile strength and hardness. This negative effect is mainly due to the nitrogen content in the steel scrap. Based on these knowledges, operating melts were realized in the foundry's operating conditions. The influence of steel scrap in the charge and the possibility of eliminating its negative effects on the properties of cast iron were investigated.

This article is aimed to study theoretical knowledges related to deep steel desulfurization and their practical application in specific production conditions. The main goal of this study was to verify the efficiency of added CaSi to processed heats in two batches, i.e., first for deep desulfurization at the beginning of the secondary metallurgy and then in a second smaller batch at the end of that process for final modification. At the beginning of the secondary metallurgy process, it was crucial to prepare a suitable chemical composition of ladle slag with advantageous properties for good assimilation of sulfur-based inclusions from desulfurization reactions. Samples were taken of final basic oxygen furnace slag, ladle slag before the deep desulfurization process at the beginning of secondary metallurgy and ladle slag at the end of processing. Detailed cleanliness analyses of steel samples taken from mold during the casting were performed using the Automated Steel Cleanliness Analyses Tool. For better understanding and interpretation of the obtained cleanliness results and their relationship, the following defined parameters were used: ratio of “Ca/Al” oxide inclusions, percentage of “liquid” inclusions and area of CaS inclusions.

The production of high-quality castings without foundry defects at minimal production costs is a constant priority for foundries. Innovation and optimization of production processes are key to achieving this goal. Computer simulation of foundry processes offers a modern alternative to expensive and time-consuming experiments in real foundries and provides a reliable representation and analysis of casting and solidification processes. A detailed analysis of the casting and solidification simulation results allows the prediction of various risks that can cause defects in cast castings, thereby reducing their quality and, last but not least, the cost of their production. The paper deals with the analysis of a computer simulation of the casting of a brake disc in the Slovak foundry. This brake disc has had shrinkages and micro shrinkages that reduce the internal quality of the casting. These defects occurred in the ribs in the upper part of the casting under the feeders. A computer simulation of the casting and solidification of this casting was made according to real conditions. It turned out that the designed ingate system with a system of feeders was not sufficient to eliminate emerging defects. A new layout of the feeders was proposed, which ultimately eliminated the occurrence of defects based on the results of computer simulation. The input parameters were set to be as close as possible to the actual needs of the foundry. 3D models of the assemblies were designed in SolidWorks CAD software, and filling and solidification simulations were performed using the NovaFlow & Solid CV 4.6r42 simulation program.