In this review, recent achievements in the application of high-entropy alloys (HEAs) and high-entropy oxides (HEOs) in the technology of solid oxide fuel cells (SOFC) are discussed for the first time. The mechanisms of the stabilization of a high-entropy state in such materials, as well as the effect of structural and charge factors on the stability of the resulting homogeneous solid solution are performed. An introduction to the synthesis methods for HEAs and HEOs is given. The review highlights such advantages of high-entropy materials as high strength and the sluggish diffusion of components, which are promising for the use at the elevated temperatures, which are characteristic of SOFCs. Application of the medium- and high-entropy materials in the hydrocarbon-fueled SOFCs as protective layers for interconnectors and as anode components, caused by their high stability, are covered. High-entropy solid electrolytes are discussed in comparison with traditional electrolyte materials in terms of conductivity. High-entropy oxides are considered as prospective cathodes for SOFCs due to their superior electrochemical activity and long-term stability compared with the conventional perovskites. The present review also determines the prioritizing directions in the future development of high-entropy materials as electrolytes and electrodes for SOFCs operating in the intermediate and low temperature ranges.

Electrolytic deposition (ELD) and electrophoretic deposition (EPD) are relevant methods for creating functional layers of solid oxide fuel cells (SOFCs). This review discusses challenges, new findings and prospects for the implementation of these methods, with the main emphasis placed on the use of the ELD method. Topical issues concerning the formation of highly active SOFC electrodes using ELD, namely, the electrochemical introduction of metal cations into a porous electrode backbone, the formation of composite electrodes, and the electrochemical synthesis of perovskite-like electrode materials are considered. The review presents examples of the ELD formation of the composite electrodes based on porous platinum and silver, which retain high catalytic activity when used in the low-temperature range (400–650 °C). The features of the ELD/EPD co-deposition in the creation of nanostructured electrode layers comprising metal cations, ceramic nanoparticles, and carbon nanotubes, and the use of EPD to create oriented structures are also discussed. A separate subsection is devoted to the electrodeposition of CeO₂-based film structures for barrier, protective and catalytic layers using cathodic and anodic ELD, as well as to the main research directions associated with the deposition of the SOFC electrolyte layers using the EPD method.

The key features and challenges of the use of electrophoretic deposition for the formation of functional layers of solid oxide fuel cells are considered. Theoretical models and experimental results of the studies of electrophoretic deposition are presented. The analysis covers the physicochemical deposition mechanisms, methods for preparing suspensions and conditions necessary for obtaining thin-film electrode and protective single- and multi-layers with both dense and porous structure for solid oxide fuel cells. The prospects of theoretical simulations of the method and its potential practical applications are evaluated. The bibliography includes 282 references.

In this work, a technology was developed for the formation of BaCe_0.8Sm_0.2O₃+1 wt% CuO (BCS-CuO)/Ce_0.8Sm_0.2O_1.9 (SDC) thin-film electrolyte membranes for intermediate-temperature solid oxide fuel cells (IT-SOFCs) on porous NiO-BCS-CuO anode substrates using direct electrophoretic deposition (EPD). The effect of increasing the zeta potential when modifying the base suspension of a micro-sized SDC-gn powder (glycine–nitrate method) with the addition of a SDC-lec nanopowder (laser evaporation–condensation) was investigated. Dependences of the current strength on the deposition time and the deposited weight on the EPD voltage were obtained, and evolution of the morphology of the coatings during the modification of the SDC-gn suspension and a suspension of BCS-CuO powder was studied. The compatibility of the shrinkage kinetics of the SDC, the BCS-CuO electrolyte coatings and the NiO-BCS-CuO anode substrate was studied during the high-temperature sintering. Dense BCS-CuO/SDC films of different thicknesses were obtained for the first time on porous NiO-BCS-CuO anode substrates and comprehensive microstructural and electrochemical studies were carried out. The developed technology can be applied to the formation of anode-supported SOFCs with thin-film electrolyte membranes.

The particle-size distribution, electrooptical potential, and acid properties of the surface of Al2O3nanoparticles in aqueous media were studied by dynamic light scattering, electroacoustic spectral...