Phosphogypsum (PG) is a waste (or by-product) of the production of phosphoric acid, a basic constituent in the manufacturing of modern fertilizers. The annual production of phosphogypsum in Tunisia is currently estimated to be 10 million tons. Its storage in slag in close proximity to production plants generates pollution problems; however, valorization may be a solution. The present paper proposes a simple process for the valorization of this by-product into a construction material. Several physicochemical characterizations are used to prove the characteristics of samples. The chemical composition shows that PG is a gypsum compound with several impurities. The morphological analyses show that the powder materials are mesoporous with a lower specific area. The structural characterizations show that these solids play the role of a water pump as the degree of hydration changes from 2 to 0 and vice versa, depending on the temperature. Mechanical and thermal analyses show that the prepared formulation is brittle and insulating, which presents opportunities for it to be used as a decoration material.

Ultrafiltration is essential for wastewater treatment, but it faces challenges such as selectivity, control, and fouling reduction. Incorporating nanoparticles into membranes enhances retention, boosts permeability, and limits fouling, improving overall performance. This study explores the properties of PVDF/Ag-ZnO composite membranes, highlighting the influence of silver-doped zinc oxide nanoparticles on membrane structure, performance, and antimicrobial effect. The non-solvent-induced phase separation (NIPS) method successfully led to the preparation of composite membranes; this method used different doses of silver-doped zinc oxide (Ag-ZnO) nanoparticles with Poly(vinylidene fluoride) (PVDF). Scanning electron microscopy (SEM), energy-dispersive X-ray spectroscopy (EDX), and water contact angle measurements were used to validate the influence of nanoparticles on the composite membrane (PVDF/Ag-ZnO) structure. Conversely, morphology (porosity, surface rigorosity), hydrophilicity, and permeability were analyzed through contact angle, image analysis, and flux measurement. In addition, the membranes were tested for antimicrobial activity against E. coli. Membrane performance shows that the incorporation of 20% w/w Ag-ZnO resulted in improved water permeability, which was about 2.73 times higher than that of a pure PVDF membrane (192.2 L·m⁻²·h⁻¹·bar⁻¹). The membrane porosity showed a linear increase with the number of NPs. The resultant asymmetric membrane was altered to increase the number of pores on the top surface by 61% and the cross-sectional pore surface by 663%. Furthermore, a high antibacterial activity of Ag-ZnO 20% was shown.