The influence of dynamic loads resulting from human motor activity and electrocorrosion inside the human body on the strength parameters of artificial joint elements has not yet been investigated. Hip joint arthroplasty is the most common surgical procedure in the world that allows doctors to remove pain and restore motor skills in people with severe hip diseases, after accidents, and in the elderly. Based on the reports, this article assesses changes in the number of implanted endoprostheses in the years 2005–2019 and determines the trends and estimated changes in the number of implanted hip prostheses in the following decades. The study assesses changes in selected strength parameters of UHMW-PE polyethylene inserts of hip joint endoprostheses during their use in the human body. The research was carried out on appropriately collected samples from UHMW-PE cups removed from the human body with a known history and lifetime from 4 to 10 years. Patients’ body weight ranged from 735 [N] to 820 [N], and the declared physical activity was similar in the entire research group. As part of the research, the values of changes in dynamic modules and the mechanical loss coefficient were determined in relation to the share of the crystalline and amorphous phases of artificial UHMW-PE cups, removed from the human body after different periods of exploitation under similar operating conditions. The analysis of selected strength parameters was performed at a temperature of 40 °C, which corresponds to the working conditions inside the human body. On the basis of numerical studies, the influence of changes in material parameters on the deformation of the artificial acetabulum during the patient’s motor activity, which is one of the causes of fatigue destruction, was determined.

The weld lines that occur in injection mouldings are critical areas on which depends on the strength of the mouldings. The flow of the material in the injection mould takes place through the gate and then gradually in the mould cavity. Depending on the shape of the formed object, the weld line may or may not occur. In the case of spreading of plastic streams or bypassing obstacles in the form of cores in the mould, the joining lines run down. Most often, the strength of the moulded part is the lowest in these areas and the resulting lines can cause cracking. The aim of the research presented in the publication was to evaluate the properties of particular parts of mouldings obtained from an experimental injection mould equipped with 4 weld line areas. The tests were performed using the method of thermal analysis by Dynamic Mechanical Analysis DMA. Tensile tests were performed on the parts with weld areas and the maximum crack force was determined. The morphology of the obtained fractures was observed using an optical microscope.

The parameters of the injection moulding process have a significant influence on the properties of the moulded parts. Selection of appropriate injection conditions (e. g. the injection temperature, mould temperature, injection and holding pressure, injection speed) contributes to the productivity and energy consumption of the injection moulding process as well as to the quality of the moulded parts. The aim of this study was to evaluate the influence of injection moulding parameters on properties of poly(ethylene) mouldings. Regranulate obtained from recycled film, which is a mixture of low-density poly(ethylene) and linear low-density poly(ethylene), was used for testing. Samples in the form of standardised tensile bars of type A1 were produced by injection moulding. A Krauss-Maffei KM65-160C4 injection moulding machine was used for this purpose. Variable parameters of the this process used in the study were: injection speed, mould temperature and holding pressure. The results of tensile strength tests of the obtained samples are presented. The weight and dimensions of mouldings from four different regranulates were also investigated. The effect of injection moulding conditions on the properties of poly(ethylene) mouldings was shown in the investigations. The mass of poly(ethylene) mouldings is dependent on the holding pressure.

The article has presented the method of 3D Digital Light Processing printing as one of the technologies used for rapid prototyping of dental models and making elements of dentures. In this work the research was presented, which the aim was to determine the effect of additional exposure time on the properties of the obtained printouts. Dynamic Mechanical Analysis test showed significant differences in stiffness between uncured specimens as well as specimens cured for 10, 20 and 30 minutes. In turn the obtained TG and DTG curves allowed to determine the most optimal curing time for DLP printouts. These studies provide the basis for determining the most appropriate method for handling printouts after the process of printing from liquid resin, so that they are the best possible quality for dentists and prosthodontists.

The injection moulding conditions may change the degree of crystallinity of the plastic to some extent, which affects the mechanical properties such as tensile strength and hardness. Moreover, the cooling conditions of the moulded parts may contribute to changes in their shrinkage. The paper presents the results of determination of the melting enthalpy of a polypropylene. The melting enthalpy ∆ Hm was determined by differential scanning calorimetry. It was found, that the value of the melting enthalpy depends on the physical conditions prevailing during the sample production process, such as the temperature of the liquid material, the cooling rate of the plastic (related to the mould temperature Tm) and the flow rate of the plastic in the mould. The degree of crystallinity of the obtained samples was also determined, which, depending on the measured enthalpy of fusion, influences the degree of structural order of the polymer. Standardized test samples were also analysed in terms of transversal shrinkage and longitudinal shrinkage. The shrinkage of the injection moulded parts results from the change of physical state of plastic during its solidification in the mould.