In recent years, partial replacement of cement with bagasse ash has been given attention for construction application due to its pozzolanic characteristics. Sugarcane bagasse ash and fine bagasse particles are abundant byproducts of the sugar industries and are disposed of in landfills. Our study presents the effect of burning bagasse at different temperatures (300 °C and 600 °C) on the compressive strength and physical properties of bagasse ash-blended mortars. Experimental results have revealed that bagasse produced more amorphous silica with very low carbon contents when it was burned at 600 °C/2 h. The compressive strength of mortar was improved when 5% bagasse ash replaced ordinary portland cement (OPC) at early curing ages. The addition of 10% bagasse ash cement also increased the compressive strength of mortars at 14 and 28 days of curing. However, none of the bagasse ash-blended portland pozzolana cement (PPC) mortars have shown improvement on compressive strength with the addition of bagasse ash. Characterization of bagasse ash was done using XRD, DTA-TGA, SEM, and atomic absorption spectrometry. Moreover, durability of mortars was checked by measuring water absorption and apparent porosity for bagasse ash-blended mortars.

Cracks in typical mortar constructions enhance water permeability and degrade ions into the structure, resulting in decreased mortar durability and strength. In this study, mortar samples are created that self-healed their cracks by precipitating calcium carbonate into them. Bacillus subtilus bacterium (10⁻⁷, 10⁻⁹ cells/mL), calcium lactate, fine aggregate, OPC-cement, water, and bagasse ash were used to make self-healing mortar samples. Calcium lactates were prepared from discarded eggshells and lactic acid to reduce the cost of self-healing mortars, and 5% control burnt bagasse ash was also employed as an OPC-cement alternative. In the presence of moisture, the bacterial spores in mortars become active and begin to feed the nutrient (calcium lactate). The calcium carbonate precipitates and plugs the fracture. Our experimental results demonstrated that cracks in self-healing mortars containing bagasse ash were largely healed after 3 days of curing, but this did not occur in conventional mortar samples. Cracks up to 0.6 mm in self-healing mortars were filled with calcite using 10⁻⁷ and 10⁻⁹ cell/mL bacteria concentrations. Images from an optical microscope, X-ray Diffraction (XRD), and a scanning electron microscope (SEM) were used to confirm the production of calcite in fractures. Furthermore, throughout the pre- and post-crack-development stages, self-healing mortars have higher compressive strength than conventional mortars. The precipitated calcium carbonates were primed to compact the samples by filling the void spaces in hardened mortar samples. When fissures developed in hardened mortars, bacteria became active in the presence of moisture, causing calcite to precipitate and fill the cracks. The compressive strength and flexural strength of self-healing mortar samples are higher than conventional mortars before cracks develop in the samples. After the healing process of the broken mortar parts (due to cracking), self-healing mortars containing 5% bagasse ash withstand a certain load and have greater flexural strength (100 kPa) than conventional mortars (zero kPa) at 28 days of cure. Self-healing mortars absorb less water than typical mortar samples. Mortar samples containing 10⁻⁷ bacteria cells/mL exhibit greater compressive strength, flexural strength, and self-healing ability. XRD and SEM were used to analyze mortar samples with healed fractures. XRD, FTIR, and SEM images were also used to validate the produced calcium lactate. Furthermore, the durability of mortars was evaluated using DTA-TGA analysis and water absorption tests.