The lack of high-performance and substantial supply of anion-exchange membranes is a major obstacle to future deployment of relevant electrochemical energy devices. Here, we select two isomers (m-terphenyl and p-terphenyl) and balance their ratio to prepare anion-exchange membranes with well-connected and uniformly-distributed ultramicropores based on robust chemical structures. The anion-exchange membranes display high ion-conducting, excellent barrier properties, and stability exceeding 8000 h at 80 °C in alkali. The assembled anion-exchange membranes present a desirable combination of performance and durability in several electrochemical energy storage devices: neutral aqueous organic redox flow batteries (energy efficiency of 77.2% at 100 mA cm⁻², with negligible permeation of redox-active molecules over 1100 h), water electrolysis (current density of 5.4 A cm⁻²at 1.8 V, 90 °C, with durability over 3000 h), and fuel cells (power density of 1.61 W cm⁻²under a catalyst loading of 0.2 mg cm⁻², with open-circuit voltage durability test over 1000 h). As a demonstration of upscaled production, the anion-exchange membranes achieve roll-to-roll manufacturing with a width greater than 1000 mm.

Anion-exchange membranes (AEMs) that can selectively transport OH^-, namely, alkaline membranes, are becoming increasingly crucial in a variety of electrochemical energy devices. Understanding the membrane design approaches can help to break through the constraints of undesired performance and lab-scale production. In this Outlook, the research progress of alkaline membranes in terms of backbone structures, synthesis methods, and related applications is organized and discussed. The evaluation of synthesis methods and description of membrane stability enhancement strategies provide valuable insights for structural design. Finally, to accelerate the deployment of relevant technologies in alkaline media, the future priority of alkaline membranes that needs to be addressed is presented from the perspective of science and engineering.

While Ru owns superior catalytic activity toward hydrogen oxidation reaction and cost advantages, the catalyst deactivation under high anodic potential range severely limits its potential to replace the Pt benchmark catalyst. Unveiling the deactivation mechanism of Ru and correspondingly developing protection strategies remain a great challenge. Herein, we develop atomic Pt-functioned Ru nanoparticles with excellent anti-deactivation feature and meanwhile employ advanced operando characterization tools to probe the underlying roles of Pt in the anti-deactivation. Our studies reveal the introduced Pt single atoms effectively prevent Ru from oxidative passivation and consequently preserve the interfacial water network for the critical H* oxidative release during catalysis. Clearly understanding the deactivation nature of Ru and Pt-induced anti-deactivation under atomic levels could provide valuable insights for rationally designing stable Ru-based catalysts for hydrogen oxidation reaction and beyond.

A new freestanding ultrathin AEMs were synthesized with high mechanical strength and anion conductivity by precise polymer topological regulation. The assembled AEMFCs have high peak power density (1.8 W cm ⁻² ) and long-term stability (∼140 h).