In recent years, the synthesis of ammonia (NH₃) has been developed by electrocatalytic technology that is a potential way to effectively replace the Haber–Bosch process, which is an industrial synthesis of NH₃. Industrial ammonia has caused a series of problems for the population and environment. In the face of sustainable green synthesis methods, the advantages of electrocatalytic nitrogen reduction for synthesis of NH₃ in aqueous media have attracted a great amount of attention from researchers. This review summarizes the recent progress on the highly efficient electrocatalysts based on 2D non-metallic nanomaterial and provides a brief overview of the synthesis principle of electrocatalysis and the performance measurement indicators of electrocatalysts. Moreover, the current development of N₂ reduction reaction (NRR) electrocatalyst is discussed and prospected.

Iron oxide nanoparticles, especially hematite (α-Fe₂O₃) and magnetite (Fe₃O₄) have attained substantial research interest in various applications of green and sustainable energy harnessing owing to their exceptional opto-magneto-electrical characteristics and non-toxicity. In this study, we synthesized high-purity hematite and magnetite nanoparticles from a facile top-down approach by employing a high-energy ball mill followed by ultrasonication. A systematic investigation was then carried out to explore the structural, morphological, thermal, optoelectrical, and magnetic properties of the synthesized samples. The experimental results from scanning electron microscopy and X-ray diffraction corroborated the formation of highly crystalline hematite and magnetite nanoparticles with average sizes of ~80 nm and ~50 nm, respectively. Thermogravimetric analysis revealed remarkable results on the thermal stability of the newly synthesized samples. The optical studies confirmed the formation of a single-phase compound with the bandgaps dependent on the size of the nanoparticles. The electrochemical studies that utilized cyclic voltammetry and electrochemical impedance spectroscopy techniques verified these iron oxide nanoparticles as electroactive species which can enhance the charge transfer process with high mobility. The hysteresis curves of the samples revealed the paramagnetic behavior of the samples with high values of coercivity. Thus, these optimized materials can be recommended for use in future optoelectronic devices and can prove to be potential candidates in the advanced research of new optoelectronic materials for improved energy devices.

The current research is focused on the chemical process and characterization of Co-based Y-type hexaferrite, electrochemically active polypyrrole doped with dodecylbenzene sulphonicacid (PPy-DBSA) and their composites. The microemulsion technique was used to produce hexaferrite with the formula Sr₂Co₂Fe₁₂O₂₂. The resistivity of pure ferrite specimens was 103 ohm-cm, which was lower than the 106 ohm-cm resistivity of the monomer utilized in the polymerization operation. As the temperature increases, the DC resistance decreases, revealing the specimens’ semiconductor nature. The cole-cole plots have been used to assess whether significant grain boundaries were involved in the dielectric relaxation process. By increasing the frequency, the electrochemical performance of all specimens was enhanced. Using the rate equation, ionic conductivity demonstrates that polarons are responsible for conduction. Because of the characteristics of the polymer PPY-conducting DBSA, the composites PPY/DBSA + Sr₂Co₂Fe₁₂O₂₂ exhibit a higher dielectric loss of 35 at 1 MHz. This specimen is perfect for electrical radiation shielding (EMI).These ferrites are widely used as permanent magnets, in microwave devices, high-density perpendicular media, and rigid disk media without lubricant and protective layers.