A novel solid-state additive manufacturing (AM) process, additive friction stir deposition (AFS-D), provides a new pathway for additively repairing damaged nonweldable aerospace materials that are susceptible to induced thermal gradients within the microstructure. In this work, we quantify the microstructural evolution and mechanical performance of an additively repaired AA7075-T651 (Al-Zn-Mg-Cu) via the AFS-D process. To evaluate the AFS-D process for repairing high strength aluminum alloys, the AFS-D technique was used to additively fill a linear groove that was machined into an AA7075-T651 plate. After repairing the plate with the AFS-D process, the repaired plate was subjected to standard T6 heat treatment. The results of this study show that the heat-treated AFS-D repair did not exhibit any significant grain growth and demonstrated an increase in the average Vickers hardness in the repair compared with the wrought 7075-T651 control. Tensile and fatigue behavior was investigated for heat-treated repair and compared with the wrought AA7075-T651 control. The heat-treated repair exhibited wrought-like tensile properties for yield stress (YS) and ultimate stress; however, the heat-treated repair had significant scatter in the elongation to failure. Additionally, the mean fatigue behavior of the heat-treated repairs displayed a reduction in cycles to failure compared with the wrought control. Lastly, a microstructure-sensitive fatigue life model was used to elucidate process-structure-property fatigue mechanism relations of the heat-treated repair and wrought AA7075.

This work presents, for the first time, an in-depth investigation of the structure–property–fatigue relationships of an Al-Mg-Si alloy (AA6061) processed via additive friction stir-deposition (AFS-D). As industry focus continues to shift for more efficient and lightweight structures, quantitative studies on the cyclic performance of additively manufactured materials are needed. In this study, the AFS-D processed AA6061-T6 was machined into specimens in two orthogonal orientations and subjected to monotonic and strain-controlled fatigue testing. The microstructural features of as-deposited AA6061 exhibited evidence of dynamic recrystallization and grain refinement. In addition, significant reduction in the intermetallic particles was observed after AFS-D processing. The fatigue results demonstrate that the as-deposited material, particularly the longitudinal direction, exhibited similar fatigue performance to wrought AA6061-T6 in both low-cycle and high-cycle fatigue regimes, which is a promising result for additively manufactured material in the as-deposited condition. By contrast, the as-deposited build direction orientation possessed slightly lower fatigue resistance than the wrought feedstock material. The AFS-D material was observed to exhibit different damage mechanisms from porosity-based damage mechanisms observed in fusion-based additively manufactured materials. Lastly, a microstructure-sensitive fatigue model was employed to capture the fatigue effects of the AFS-D processing on the AA6061.