In this study, plasma gas species and temperature were varied to evaluate the reactive species produced and the bactericidal effect of plasma. Nitrogen, carbon dioxide, oxygen, and argon were used as the gas species, and the gas temperature of each plasma was varied from 30 to 90 °C. Singlet oxygen, OH radicals, hydrogen peroxide, and ozone generated by the plasma were trapped in a liquid, and then measured. Nitrogen plasma produced up to 172 µM of the OH radical, which was higher than that of the other plasmas. In carbon dioxide plasma, the concentration of singlet oxygen increased from 77 to 812 µM, as the plasma gas temperature increased from 30 to 90 °C. The bactericidal effect of carbon dioxide and nitrogen plasma was evaluated using bactericidal ability, which indicated the log reduction per minute. In carbon dioxide plasma, the bactericidal ability increased from 5.6 to 38.8, as the temperature of the plasma gas increased from 30 to 90 °C. Conversely, nitrogen plasma did not exhibit a high bactericidal effect. These results demonstrate that the plasma gas type and temperature have a significant influence on the reactive species produced and the bactericidal effect of plasma.

The purpose of this study was to investigate the effect of gas species used for low-temperature atmospheric pressure plasma surface treatment, using various gas species and different treatment times, on zirconia surface state and the bond strength between zirconia and dental resin cement. Three groups of zirconia specimens with different surface treatments were prepared as follows: untreated group, alumina sandblasting treatment group, and plasma treatment group. Nitrogen (N₂), carbon dioxide (CO₂), oxygen (O₂), argon (Ar), and air were employed for plasma irradiation. The bond strength between each zirconia specimen and resin cement was compared using a tension test. The effect of the gas species for plasma irradiation on the zirconia surface was investigated using a contact angle meter, an optical interferometer, an X-ray diffractometer, and X-ray photoelectric spectroscopy. Plasma irradiation increased the wettability and decreased the carbon contamination on the zirconia surface, whereas it did not affect the surface topography and crystalline phase. The bond strength varied depending on the gas species and irradiation time. Plasma treatment with N₂ gas significantly increased bond strength compared to the untreated group and showed a high bond strength equivalent to that of the sandblasting treatment group. The removal of carbon contamination from the zirconia surface and an increase in the percentage of Zr-O₂ on the zirconia surface by plasma irradiation might increase bond strength.

The aim of the study was to design and build a multi-gas temperature-controllable plasma jet that can control the gas temperature of plasmas with various gas species, and evaluated its temperature control performance. In this device, a fluid at an arbitrary controlled temperature is circulated through the plasma jet body. The gas exchanges heat with the plasma jet body to control the plasma temperature. Based on this concept, a complex-shaped plasma jet with two channels in the plasma jet body, a temperature control fluid (TCF) channel, and a gas channel was designed. The temperature control performance of nitrogen gas was evaluated using computational fluid dynamics analysis, which found that the gas temperature changed proportionally to the TCF temperature. The designed plasma jet body was fabricated using metal 3D-printer technology. Using the fabricated plasma jet body, stable plasmas of argon, oxygen, carbon dioxide, and nitrogen were generated. By varying the plasma jet body temperature from −30 °C to 90 °C, the gas temperature was successfully controlled linearly in the range of 29–85 °C for all plasma gas species. This is expected to further expand the range of applications of atmospheric low temperature plasma and to improve the plasma treatment effect.

Atmospheric-pressure plasma-enhanced chemical vapor deposition (AP-PECVD) enables low-temperature coating in open air, yet the interplay between precursor activation and ambient-derived species remains unclear. Here, thin films from an amine precursor are deposited using a helium plasma and characterized by gas chromatography–mass spectrometry (GC-MS), a quartz crystal microbalance (QCM), and X-ray photoelectron spectroscopy (XPS). GC-MS indicates partial precursor conversion and formation of oxygen- and nitrogen-containing products, consistent with participation of ambient air and moisture. QCM identifies a limited precursor-concentration window in which mass increases monotonically during plasma exposure and remains constant after shutdown; outside this window, post-discharge mass loss occurs, indicating desorption of weakly bound species. XPS confirms carbon-rich films incorporating oxygen- and nitrogen-containing functionalities and complete substrate coverage at higher precursor concentrations.