In the present article the doping of aluminide coatings by Pt/Pd as well as Hf or Pd using industrial processes was developed. The different combinations of doping elements were tested as well as their influence on chemical composition of coatings was initially investigated. The Pt and Pd and both Pt + Pd was electroplated on the surface of the MAR M247 nickel superalloy. The Zr or Hf was doped during low activity CVD aluminizing process using industrial Bernex BPX Pro 325S system. The conducted research showed that Pt and Pd formed the (Ni, Pd, Pt) Al solid solution in the outer additive layer. The higher concentration of palladium in the near surface and in the whole additive layer was detected. The platinum was presented below the surface of aluminide coating. The Zr or Hf was detected mainly in the diffusion zone. The low concentration of Zr (about 0.1 wt.%) in the outer zone was observed. The hafnium was detected mainly in the diffusion zone but in the outer additive layer a small concentration of this element was measured. The obtained results showed that formation of three elements (Pd, Pt) + Zr or Hf modified aluminide coating using proposed technology is possible. The structure of all obtained aluminide coatings was typical for a low-activity, high temperature (LAHT) formation process mainly by outward diffusion of Ni from base material.

In the article, the new concept of plasma-sprayed coatings for the cylinder liner was presented. The new type of powder containing WC-CrC-Ni with a 5 and 10 wt. % addition of nano-YSZ powder was plasma-sprayed on aluminum 2017 alloy samples. The selection of optimal plasma-spraying parameters was made taking into account the thickness, porosity, and hardness of the coatings. For the coatings obtained according to the developed parameters, the analysis of their microstructure, chemical, and phase composition was performed. At the next stage, the friction coefficient of the developed coatings was tested and compared with the properties of a classic cast-iron cylinder liner. The obtained results suggest that the developed type of coating might be used for cylinder liner applications after a deeper friction analysis.

The erosion resistance of materials against solid particles is a very important property, especially in the transportation of powders or in aeronautics (dust inside jet engines). There is a strong need to introduce new materials that have higher solid particle erosion resistance than state-of-the-art materials. Thus, in the present work, the solid erosion particles of high entropy alloys (HEAs) based on the Al0.7CoCrFeNi matrix were studied compared to the state-of-the-art stainless steel AISI 304. Furthermore, the effect of the addition of Ti to HEAs on hardness and erosion resistance was investigated. Current research included the development of the chemical composition of a new kind of HEA designed on the basis of thermodynamical calculations performed in CALPHAD, its manufacturing, full characterization involving microstructural and phase analyses, hardness measurements, solid particle erosion tests, and finally, the elucidation of erosion mechanisms. It was found that HEAs showed higher hardness as well as erosion resistance than AISI 304. Moreover, it was found that the increase in Ti content in an HEA resulted in an increase in the hardness and resistance to the erosion of the studied HEA. As the main reason for this phenomenon, the stabilization of the β-BCC phase, suppression of the α-FCC phase, and the appearance of the Ni₃Ti phase in the studied HEA were claimed.

Sciendo provides publishing services and solutions to academic and professional organizations and individual authors. We publish journals, books, conference proceedings and a variety of other publications.

A patient’s body accepting a bone implant depends not only on the biomaterial used, but also on its surface, which allows it to properly interact with bone cells. Therefore, research has focused on improving the bioactive and tribological properties of titanium and its alloys. Commercially pure titanium (cp-Ti) is widely used as a biomedical material. However, it is characterized by unsuitable tribological properties. In this work, yttria-stabilized zirconia (YSZ) was deposited on a cp-Ti substrate via plasma spray–physical vapor deposition (PS-PVD). The structural characteristics were determined using X-ray analysis (XRD). Additionally, the lattice parameters of each phase were determined using Rietveld’s method. High-resolution scanning microscopy (HR-SEM) showed a typical column structure of coatings that can be used with PS-PVD. Depending on the process parameters, the coatings differed in thickness in the range of 2.4–9.0 µm. The surface roughness also varied. The samples were subjected to nano-indenter testing. A slight change in hardness after deposition of the coating was observed, in addition to a significant decrease in the Young’s modulus. The Young’s modulus in relation to the metallic substrate was reduced to 58 or 78 GPa depending on the parameters of the spray-coating process.

The diffusion boriding process allows to increase the abrasion and corrosion resistance of the majority of steel grades. The aim of this study was to determine the influence of the chemical composition of the substrate of various steel grades ...