It is challenging to purify oily wastewater, which affects water-energy-food production. One promising method is membrane-based separation. This paper reviews the current research trend of applying cellulose as a membrane material that mimics one of three typical biostructures: superhydrophobic, underwater superoleophobic, and Janus surfaces. Nature has provided efficient and effective structures through the evolutionary process. This has inspired many researchers to create technologies that mimic nature’s structures or the fabrication process. Lotus leaves, fish scales, and Namib beetles are three representative structures with distinct functional and surface properties: superhydrophobic, underwater superoleophobic, and Janus surfaces. The characteristics of these structures have been widely studied and applied to membrane materials to improve their performance. One attractive membrane material is cellulose, whichhas been studied from the perspective of its biodegradability and sustainability. In this review, the principles, mechanisms, fabrication processes, and membrane performances are summarized and compared. The theory of wettability is also described to build a comprehensive understanding of the concept. Finally, future outlook is discussed to challenge the gap between laboratory and industrial applications.

Membrane bioreactor (MBR) deteriorates due to fouling on the membrane pores, which can reduce the membrane performance. To reduce membrane fouling, the addition of inorganic filler can enhance the antifouling properties. This study investigates two different membrane preparation by thermally induced phase separation (TIPS) and dip coating methods to modify hollow fiber membrane with Silver Nanoparticles (AgNPs)-Zeolites used in MBR for industrial wastewater treatment. Performance was evaluated by analyzing the flux of water and wastewater, rejection, water content, and antifouling properties. Characterization result represented the synthesized silver nanoparticles had similar diffraction peak with commercial AgNPs, then the micrograph of AgNPs and zeolites addition membrane showed that the inorganic material had an octahedral shape representing zeolite crystal and irregular shape representing AgNPs. The addition of zeolites and AgNPs resulted in satisfying performance, increased flux, rejection, and antifouling properties.

The two types of cellulose nanofiber (CNF) surface characteristics were evaluated by oil contact angle under ethanol–water solution at several concentrations as well as in air. Wood pulp-based 2,2,6,6-tetramethylpiperidine-1-oxylradical (TEMPO)-oxidized cellulose nanofiber (TOCNF) sheets and bamboo-derived mechanical counter collision cellulose nanofiber (ACC-CNF) sheets were fabricated by casting followed by drying. The CNF shows underwater superoleophobic mimicking fish skin properties and slippery surface mimicking Nepenthes pitcher. The underwater superoleophobic properties of CNF was evaluated theoretically and experimentally. The theoretical calculation and experimental results of contact angle showed a large deviation. The roughness, zeta potential, and water absorption at different concentrations were key factors that determine the deviation. Antifouling investigation revealed that CNF was a good candidate for antifouling material.

The competitive reactions of lignocellulose hydrolysis and monosaccharide degradation in the subcritical water (SCW) hydrolysis of coconut husk were investigated to optimize the reducing sugar yield. Optimization analysis was performed by response surface methodology (RSM) and kinetics studies. Parameters of process optimization were varied at 130-170 °C for 15-45 min. The reducing sugars were measured using the Dinitro salicylic acid method. The sugar yield increased when the temperature increased from 130 °C to 170 °C. The highest reduction sugar yield of 4.946 g/L was obtained at 183.6 °C for 4.8 min and 23.4 liquid/solid ratio (LSR). Kinetics studies were carried out at temperature variations of 150, 170, and 190 °C and pressures of 60, 80, and 100 bar for 5 to 60 min. The yield of reducing sugar decreased with increasing temperature. The kinetic model 2B is the best method to explain the competitive reaction kinetics of coconut husk hydrolysis. This research is an innovation to increase the reducing sugar to make the process more commercially viable. Copyright © 2022 by Authors, Published by BCREC Group. This is an open access article under the CC BY-SA License (https://creativecommons.org/licenses/by-sa/4.0).