In order to obtain high-performance aluminum alloy parts fabricated by selective laser melting, this paper investigates the relationship between the process parameters and microstructure properties of AlSi10Mg. The appropriate process parameters are obtained: the layer thickness is 0.03 mm, the laser power is 370 W, the scanning speed is 1454 mm/s, and the hatch spacing is 0.16 mm. With these process parameters, the ultimate tensile strength of the as-printed status is 500.7 ± 0.8 MPa, the yield strength is 311.5 ± 5.9 MPa, the elongation is 7.7 ± 0.5%, and the relative density is 99.94%. After annealing treatment at 275 °C for 2 h, the ultimate tensile strength is 310.8 ± 1.3 MPa, the yield strength is 198.0 ± 2.0 MPa, and the elongation is 13.7 ± 0.6%. The mechanical properties are mainly due to the high relative density, supersaturate solid solution, and fine dispersed Si. The supersaturate solid solution and nano-sized Si formed by the high cooling rate of SLM. After annealing treatment, the Si have been granulated and grown significantly. The ultimate tensile strength and yield strength are reduced, and the elongation is significantly improved.

High-entropy alloy (HEA) is a new type of multi-principal alloy material and the Hf-Nb-Ta-Ti-Zr HEAs have attracted more and more attention from researchers due to their high melting point, special plasticity, and excellent corrosion resistance. In this paper, in order to reduce the density of the alloy and maintain the strength of the Hf-Nb-Ta-Ti-Zr HEAs, the effects of high-density elements Hf and Ta on the properties of HEAs were explored for the first time based on molecular dynamics simulations. A low-density and high-strength Hf_0.25NbTa_0.25TiZr HEA suitable for laser melting deposition was designed and formed. Studies have shown that the decrease in the proportion of Ta element reduces the strength of HEA, while the decrease in Hf element increases the strength of HEA. The simultaneous decrease in the ratio of Hf and Ta elements reduces the elastic modulus and strength of HEA and leads to the coarsening of the alloy microstructure. The application of laser melting deposition (LMD) technology refines the grains and effectively solves the coarsening problem. Compared with the as-cast state, the as-deposited Hf_0.25NbTa_0.25TiZr HEA obtained by LMD forming has obvious grain refinement (from 300 μm to 20–80 μm). At the same time, compared with the as-cast Hf_0.25NbTa_0.25TiZr HEA (σ_s = 730 ± 23 MPa), the as-deposited Hf_0.25NbTa_0.25TiZr HEA has higher strength (σ_s = 925 ± 9 MPa), which is similar to the as-cast equiatomic ratio HfNbTaTiZr HEA (σ_s = 970 ± 15 MPa).

In this paper, the cracking of Al-Mn-Mg-Sc-Zr alloys prepared by selective laser melting (SLM) was comprehensively explored and the influence of process parameters on the generation and propagation of cracks was deeply studied. It was found that the higher laser power and volume energy density will lead to a decrease in the relative density of the material. The lower laser power or volume energy density will lead to cracking of the alloy. The microstructure analysis indicated that plenty of manganese-rich second phases precipitated at the bottom of the melt pool, which increased the tendency of cracking occurred at the bottom of the melt pool. Through the optimization of the process parameters, the SLM forming process parameters of the Al-5.22Mn-1.16Mg-0.81Sc-0.46Zr alloy are successfully obtained, and the crack-free tensile samples are prepared. The microstructure and mechanical properties of the as-deposited aluminum-manganese alloy is analyzed. The bottom and inside of the melt pool are equiaxed grains. The size of the equiaxial grains at the bottom of the melt pool is less than 2 μm, and the coarse equiaxial grains inside the melt pool are approximately 5 μm. As-deposited alloy has a room temperature tensile strength of 455.2 ± 0.7 MPa and elongation of 15.4 ± 0.3%. This study provides guidance for selective laser melting forming of high-strength aluminum-manganese alloy parts, and promotes the industrial production of high-strength aluminum alloy near net forming complex parts.

Research on the development of new lightweight Al–Li alloys using a selective laser melting process has great potential for industrial applications. This paper reports on the development of novel aluminum–lithium alloys using selective laser melting technology. Al–Cu–Li–Mg–Ag–Sc–Zr pre-alloyed powders with lithium contents of 1 wt.%, 2 wt.% and 3 wt.%, respectively, were prepared by inert gas atomization. After SLM process optimization, the microstructure and mechanical properties of the as-printed specimens were investigated. The densifications of the three newly developed alloys were 99.51%, 98.96% and 92.01%, respectively. They all had good formability, with the lithium loss rate at about 15%. The as-printed alloy with 1% Li content presented good comprehensive properties, with a yield strength of 413 ± 16 MPa, an ultimate tensile strength of 461 ± 12 MPa, and an elongation of 14 ± 1%. The three alloys exhibited a layered molten pool stacking morphology and had a typical heterostructure. The columnar crystals and equiaxed fine grains were alternately arranged, and most of the precipitated phases were enriched at the grain boundaries. The change in Li content mainly affected the precipitation of the Cu-containing phase. When the Li content was 1 wt.%, the following occured: θ phase, T₁ phase and T_B phase. When Li increased to 2 wt.%, T₁ and T₂ phases precipitated together. When Li reaches 3 wt.%, δ’ phase precipitated with T₂ phase. This study provides useful guidance for the future SLM forming of new crack-free and high-strength Al–Li alloys.

Rare earth (RE) additions are capable of refining the α-Al phase as well as modifying the eutectic Si particles of alloys. The cooling rate in casting process should be carefully concerned when the Al-Si alloys are refined and modified by adding RE elements. In this study, the effect of cooling rates on the microstructure and mechanical properties of La modified Al-7.0Si-0.3Mg alloys was studied in gravity die casting and semi-solid die casting. It is found that in La modified Al-7.0Si-0.3Mg alloys, with increasing the cooling rate from 0.2 to 9 K/s in gravity die casting, the α-Al grains are greatly refined and the Si particles are modified to branching morphology, which evidently increases the UTS and elongation of alloys. In addition, when increasing the cooling rate from 30 to 130 K/s in semi-solid die casting, the α-Al grains are refined from 140 to 47 μm, and the Si particles are modified to fibrous morphology, which increases the UTS from 190 to 230 MPa and elongation from 10% to 11%. However, the 0.4 wt.% La addition results to La-rich phases formed in microstructure, which impairs the mechanical properties of Al-7.0Si-0.3Mg alloys in semi-solid die casting.