In order to obtain high-performance aluminum alloy parts fabricated by selective laser melting, this paper investigates the relationship between the process parameters and microstructure properties of AlSi10Mg. The appropriate process parameters are obtained: the layer thickness is 0.03 mm, the laser power is 370 W, the scanning speed is 1454 mm/s, and the hatch spacing is 0.16 mm. With these process parameters, the ultimate tensile strength of the as-printed status is 500.7 ± 0.8 MPa, the yield strength is 311.5 ± 5.9 MPa, the elongation is 7.7 ± 0.5%, and the relative density is 99.94%. After annealing treatment at 275 °C for 2 h, the ultimate tensile strength is 310.8 ± 1.3 MPa, the yield strength is 198.0 ± 2.0 MPa, and the elongation is 13.7 ± 0.6%. The mechanical properties are mainly due to the high relative density, supersaturate solid solution, and fine dispersed Si. The supersaturate solid solution and nano-sized Si formed by the high cooling rate of SLM. After annealing treatment, the Si have been granulated and grown significantly. The ultimate tensile strength and yield strength are reduced, and the elongation is significantly improved.

HfNbTaTiZr high-entropy alloy has wide application prospects as a biomedical material, and the use of laser additive manufacturing can solve the forming problems faced by the alloy. In view of the characteristics of the one-time forming of additive manufacturing methods, it is necessary to develop non-mechanical processing modification methods. In this paper, deep cryogenic treatment (DCT) is first applied to the modification of a HEA with BCC structure, then the post-processing method of DCT is combined with laser melting deposition (LMD) technology to successfully realize the coordinated improvement of forming and strength–ductility synergistic improvement in lightweight Hf_0.25NbTa_0.25TiZr alloy. The final tensile strength of the alloy after DCT treatment is 25% higher than that of the as-cast alloy and 11% higher than that of the as-deposited alloy, and the elongation is increased by 48% and 10%, respectively. In addition, DCT also achieves induced phase transition without additional deformation.