Conducting polymer fillers are added to a Bi₂Te₃matrix to develop an inorganic/organic composite including the interface, where an energy filtering effect occurs along with phonon scattering, resulting in greatly enhanced thermoelectric performance.

Powder bed 3D printing can be applied to sandcasting mold manufacturing to ensure high quality and economy through process innovation. In this study, refractory alumina cement was used as an aqueous binder to ensure high-temperature thermal stability to minimize the addition of organic matter to reduce gas generation. In addition, spherical silica sand, the study material, was selected to a size of 30 µm to improve the casting mold resolution. To improve the surface quality through the post-treatment process, we confirmed the change in the surface roughness of the mold depending on the surface treatment of colloidal silica and the presence or absence of heat treatment, and finally made the mold through actual casting. Changes in the surface roughness and flowability of the cast body after mold post-treatment were confirmed. For aluminum castings, the shrinkage rate and surface roughness were confirmed in a box-shaped mold via gravity casting, and the flowability of the molten metal in the mold was confirmed in a hand-shaped mold. There was a change in the roughness and porosity of the mold, owing to the post-treatment, and the influence of the surface roughness and flowability of the cast body during actual casting was confirmed.