Powder bed 3D printing can be applied to sandcasting mold manufacturing to ensure high quality and economy through process innovation. In this study, refractory alumina cement was used as an aqueous binder to ensure high-temperature thermal stability to minimize the addition of organic matter to reduce gas generation. In addition, spherical silica sand, the study material, was selected to a size of 30 µm to improve the casting mold resolution. To improve the surface quality through the post-treatment process, we confirmed the change in the surface roughness of the mold depending on the surface treatment of colloidal silica and the presence or absence of heat treatment, and finally made the mold through actual casting. Changes in the surface roughness and flowability of the cast body after mold post-treatment were confirmed. For aluminum castings, the shrinkage rate and surface roughness were confirmed in a box-shaped mold via gravity casting, and the flowability of the molten metal in the mold was confirmed in a hand-shaped mold. There was a change in the roughness and porosity of the mold, owing to the post-treatment, and the influence of the surface roughness and flowability of the cast body during actual casting was confirmed.

With the development of the powder bed 3D printing process, sand casting can be performed with methods that are more advanced than the traditional ones, thus enabling new research on applied materials. When sand is 3D-printed with cement as a binder, its casting performance is improved and sufficient thermal stability of conventional organic and inorganic binders is ensured. In this study, to ensure high resolution and strength in a physical and simple mixture of cement and sand, the compatibility for casting was confirmed using submicron-level cement with ingredients and sizes similar to commercial sand, which is uniformly controlled at 4 µm, instead of conventional sand. To enable quick 3D printing, calcium aluminate cement, which has quick binding properties, was used for high-temperature casting. The strength up to 6 h after hydration was compared to determine the curing rate of silica, mullite, and alumina sand containing cement components. By investigating the change in strength due to heat treatment and comparing the adhesion drop test results after powder bed formation, the material containing silica sand was determined as the most suitable for powder layer 3D printing for application to the mold.