In this work, a two-stage methodology to design super-hydrophobic surfaces was proposed. The first step consists of creating a rough nano/micro-structure and the second step consists of reducing the surface energy using octadecyltrimethoxysilane. The surface roughening was realized by three different short-term pretreatments: (i) Boiling water, (ii) HNO₃/HCl etching, or (iii) HF/HCl etching. Then, the surface energy was reduced by dip-coating in diluted solution of octadecyltrimethoxysilane to allow the formation of self-assembled silane monolayers on a 6082-T6 aluminum alloy surface. Super-hydrophobic aluminum surfaces were investigated by SEM-EDS, FTIR, profilometry, and contact and sliding angles measurements. The resulting surface morphologies by the three approaches were structured by a dual hierarchical nano/micro-roughness. The surface wettability varied with the applied roughening pretreatment. In particular, an extremely high water contact angle (around 180°) and low sliding angle (0°) were evidenced for the HF/HCl-etched silanized surface. The results of electrochemical tests demonstrate a remarkable enhancement of the aluminum alloy corrosion resistance through the proposed superhydrophobic surface modifications. Thus, the obtained results evidenced that the anti-wetting behavior of the aluminum surface can be optimized by coupling an appropriate roughening pretreatment with a self-assembled silane monolayer deposition (to reduce surface energy) for anticorrosion application.

Dental implant biomaterials are expected to be in contact with living tissues, therefore their toxicity and osseointegration ability must be carefully assessed. In the current study, the wettability, cytotoxicity, and genotoxicity of different alumina–zirconia–titania composites were evaluated. The surface wettability determines the biological event cascade in the bioceramic/human living tissues interface. The measured water contact angle indicated that the wettability strongly depends on the ceramic composition. Notwithstanding the contact angle variability, the ceramic surfaces are hydrophilic. The cytotoxicity of human gingival fibroblast cells with materials, evaluated by an (3-(4,5 methylthiazol-2-yl)-2,5-diphenyl-tetrazolium bromide (MTT) test, revealed an absence of any cytotoxic effect. A relationship was found between the cell viability and the wettability. It was subsequently deduced that the cell viability increases when the wettability increases. This effect is more pronounced when the titania content is higher. Finally, a comet test was applied as complementary biocompatibility test to detect any changes in fibroblast cell DNA. The results showed that the DNA damage is intimately related to the TiO₂ content. Genotoxicity was mainly attributed to ceramic composites containing 10 wt.% TiO₂. Our research revealed that the newly developed high performance alumina–zirconia–titania ceramic composites contain less than 10 wt.% TiO₂, and display promising surface properties, making them suitable for dental implantology applications.

In this paper, a sol-gel N-propyl-trimethoxy-silane coating filled with different amount of multi-wall carbon nanotubes (MWCNTs) was investigated in order to improve the aluminum corrosion resistance. The nanocomposite coating was applied, by drop casting, on AA6061 aluminum alloy substrate. The morphological analysis highlighted that a uniform sol-gel coating was obtained with 0.4 wt.% CNT. Lower or higher nanotube contents lead to the formation of heterogeneities or agglomeration in the coating, respectively. Furthermore, all nanocomposite coatings exhibited effective adhesion to the substrate. In particular, the pull-off strength ranged in 0.82–1.17 MPa. Corrosion protection of the aluminum alloy in NaCl 3.5 wt.% electrolyte (seawater) was significantly improved after CNT addition to the base coating. The stability in electrochemical impedance was observed during three days of immersion in the sodium chloride solution. AS3-CNT2 and AS3-CNT4 batches showed advanced electrochemical stability during immersion tests. Furthermore, interesting results were evidenced in potentiodynamic polarization curves where a decrease of the corrosion current of at least two order of magnitude was observed. Moreover, the breakdown potential was shifted toward noble values. Best results were observed on AS3-CNT6 specimen which exhibited a passivation current density of approximately 1.0 × 10⁻⁵ mA/cm² and a breaking potential of 0.620 V/AgAgCl_sat.