In order to improve the properties of calcium sulfate anhydrous whisker (ACSW) and polyester fiber composite reinforced asphalt mixture (ACPRA) to meet the service requirements of pavement materials in low-temperature environments, the central composite circumscribed design (CCC), a kind of response surface methodology, was chosen to optimize the design parameters. Three independence variables, asphalt aggregate ratio, ACSW content, and polyester fiber content were adopted to evaluate the design parameters. Four responsive variables, air voids, Marshall stability, splitting tensile strength, and failure tensile strain, were chosen to study the volumetric and mechanical characteristics, and the low-temperature behavior of ACPRA by the Marshall test and indirect tensile test at −10 °C. The results showed that, taking low-temperature behavior optimization as the objective, the CCC method was practicable to optimize design of ACPRA, and the optimization design parameters were asphalt aggregate ratio of 4.0%, ACSW content of 10.8%, and polyester fiber content of 0.4%. Furthermore, the impact of three independence variables interactions on four response variables was also discussed, and it was identified that the interaction between asphalt aggregate ratio and ACSW content, and between asphalt aggregate ratio and polyester fiber content, has greater bearing on the splitting tensile strength and failure tensile strain of APCRA. Meanwhile, ACSW and polyester fiber enhancing the low-temperature behavior of APCRA was primarily connected with their contents.

Asphalt mastic, which consists of an asphalt binder and a mineral filler, provides critical adhesion and viscoelasticity to an asphalt mixture. The rheological response of the asphalt mastic is mainly derived from its asphalt binder. In this study, a simple laboratory test method is proposed to estimate the relationship of asphalt binder and its mastic. Two modified binders (3.5% and 4.0% styrene–butadiene–styrene (SBS) of asphalt binder by mass) were blended with a limestone filler at six different mineral filler contents to produce mastic samples. A modified multiple stress creep-recovery (MSCR) test was conducted on both the asphalt binder and its mastic with the same testing protocols, and the stress conditions and rheological response of asphalt binder in the mastic with linear or nonlinear viscoelasticity were both investigated. The results show that the stress of the asphalt binder in its mastic decreased with increasing filler contents. However, for the linear-viscoelasticity mastic, the decrease rate of the stress began to slow down when the filler content had reached 100% or 120%. For the rheological properties of the asphalt binder in the mastic, the %R of the asphalt binder was improved by adding filler, especially for the nonlinear-viscoelasticity mastic. The asphalt binder of the linear-viscoelasticity asphalt mastic also showed a linear viscoelastic response and a good recovery property. The performance of the asphalt mastic and rheological properties of its asphalt binder were highly related to its filler content.

Incorporating iron tailings (ITs) into asphalt represents a new method for waste-to-resource conversion. The objective of this study is to evaluate the fatigue performance of ITs as fillers in asphalt mastic and investigate the interaction and interfacial adhesion energy between asphalt and ITs. To achieve that, the particle size distributions of two ITs and limestone filler (LF) were tested through a laser particle size analyzer; the morphology and structure characteristics were obtained by scanning electronic microscopy (SEM), the mineral compositions were conducted through X-ray diffraction (XRD), and the chemical compositions were tested through X-ray Fluorescence Spectrometer (XRF). Furthermore, the fatigue properties of asphalt mastic and the interaction between asphalt binder and mineral fillers (ITs and LFs) were evaluated by Dynamic Shear Rheometer (DSR). The interfacial adhesion energy between ITs and asphalt binder were calculated through molecular dynamics simulation. In the end, the correlation between the test results and the fatigue life is established based on the gray correlation analysis, the environmental and economic benefits of iron tailings asphalt pavement are further evaluated. The results show that the particle size distribution of ITs is concentrated between 30 μm and 150 μm, and the main component is quartz. ITs have rich angularity and a higher interaction ability with asphalt. The adhesion energy of iron tailings filler to asphalt is less than that of limestone. The correlation degree of the interfacial adhesion energy and interaction between asphalt and mineral filler with asphalt mastic fatigue life is close to 0.58. Under the combined action of interaction ability and interfacial adhesion energy, the fatigue life of IT asphalt mastic meets the requirements. ITs as a partial replacement for mineral fillers in asphalt pavement have great environmental and social effectiveness.

High-Content Crumb Rubber Asphalt (HCRA) binder improves road performance and address waste tyre pollution, yet its ageing behaviour is not fully understood. In this study, 70# neat asphalt binder and HCRA with rubber contents of 35% and 50% were selected and aged through the Thin Film Oven Test (TFOT) and Pressure Ageing Vessel (PAV) tests. FTIR (Fourier Transform Infrared Spectroscopy) and DSR (Dynamic Shear Rheometer) were employed to investigate their chemical composition and rheological properties. The FTIR results show that HCRA’s chemical test results are similar to those of 70#, but HCRA is more susceptible to ageing. I(C=C) strength decreases with age. The DSR results show that HCRA outperforms 70# neat asphalt binder in terms of viscoelasticity, high temperature performance and fatigue resistance, and exhibits greater resistance to ageing. The ageing index (AI) was obtained through a calculation using the formula, and overall, 70# neat asphalt binder is more sensitive to ageing behaviour and less resistant to ageing, and HCRA is particularly outstanding for fatigue resistance. A strong correlation is observed between chemical composition and some rheological property indicators. Therefore, we are able to predict the rheological properties using chemical composition indicators. This study provides insight into the ageing behaviour of a neat asphalt binder and an HCRA binder and demonstrates that the HCRA binder outperforms conventional asphalt in several performance areas. It also provides theoretical support for the consumption of waste tyres to prepare high content crumb rubber asphalt.

The performance of an asphalt mixture is significantly affected by the properties of its asphalt mortar, which consists of an asphalt binder, mineral fillers, fine aggregates and air voids. The aim of this work was to evaluate the correlations between the high-temperature performance of an asphalt mixture and the rheological properties of its corresponding asphalt mortar. The multisequence repeated loading (MSRL) test was used to estimate the high-temperature performance of the asphalt mixture. Six different gradations, AC-13, SMA-13, SUP-13, AC-20, SUP-20 and AC-25, and two styrene–butadiene–styrene (SBS)-modified asphalt binders were considered and used to prepare the asphalt mixture specimens. The gradations and asphalt types of asphalt mortars were consistent with their asphalt mixtures. A modified multiple-stress creep–recovery (MSCR) test was proposed for evaluating the rheological properties of asphalt mortar with a dynamic shear rheometer (DSR). Based on the basic form of the Hirsh model, a multiple regression model was established, and its coefficient of determination (R-square) was 0.96. The rheological response of the asphalt mortar presented great correlation with the high-temperature behaviour of the asphalt mixture. In addition, the MSCR indicators (nonrecoverable compliance and percent recovery) obtained at 12.8 kPa creep stress represented the rheological status of asphalt mortar in asphalt mixture well. Therefore, the mechanical behaviours of asphalt mixture at high temperature could be accurately predicted by the MSCR indicators of asphalt mortar and its coarse aggregate parameters.

Asphalt bridge deck pavement is a weak bridge structure area, and early damage usually occurs in this area under vehicle loads. Due to the complexity and diversity of vehicle loads and material structures, it is difficult to truly reflect the mechanical response of bridge deck pavement under vehicle loads. This paper studies the vehicle road interaction from a microscopic perspective. In this research, the dynamic response of asphalt bridge deck pavement under multiple loads is comparatively studied, considering the mesoscopic structure of the asphalt materials. First, the compressive properties, tensile properties and interlaminar shear properties of each layer were studied through laboratory tests. Second, the asphalt mixture bridge deck pavement model, including mesostructured, was established. Then, the subprograms of the sinusoidal vibration load, rolling load and vehicle road coupling load were realised using the discrete element method (DEM). Finally, the mesomechanical response of asphalt bridge deck pavement under those three dynamic loads was comparatively studied. The study finds that there is a large difference in the mechanical response of bridge deck pavement under multiple loads. A sinusoidal vibration load can simply be the moving load, the edge of the loading area and the bottom of the lower layer bear large tensile stress, and the shear stress at the edge of the loading area is approximately 4 times that of the middle area. The rolling load can better reflect the status of the vehicle. There is a certain difference in the shear stress response between the rolling load and the sinusoidal vibration load, and the lower layer bears compressive–tensile alternating stress. Under the vehicle road coupling load, the volatility of the dynamic response is obvious due to the road roughness. Therefore, it is of vital importance to improve the abrasion resistance of the surface layer. The results show that the comprehensive consideration of multiple loads and the mesostructure can provide a more reliable method for the dynamic design of bridge deck pavement, which is of great significance for improving the durability of the pavement.