Bamboo is much more easily attacked by fungus compared with wood, resulting in shorter service life and higher loss in storage and transportation. It has been long accepted that the high content of starch and sugars in bamboo is mainly responsible for its low mould resistance. In this paper, acetic acid, propionic acid, oxalic acid, citric acid, and hydrochloric acid were adopted to hydrothermally hydrolyze the starch in bamboo, with the aims to investigate their respective effect on the mould and blue-stain resistance of bamboo, and the optimized citric acid in different concentrations were studied. The starch content, glucose yields, weight loss, and colour changes of solid bamboo caused by the different acidic hydrolysis were also compared. The results indicated that weak acidic hydrolysis treatment was capable of improving mould-resistant of bamboo. The mould resistance increased with the increased concentration of citric acid. Bamboo treated with citric acid in the concentration of 10% could reduce the infected area ranging to 10–17%, the growth rating of which could reach 1 resistance. The content of soluble sugar and starch remained in bamboo decreased significantly from 43 mg/g to 31 mg/g and 46 mg/g to 23 mg/g, respectively, when the citric acid concentration varied from 4% to 10%. Citric acid treatments of 10% also caused a greatest surface colour change and weight loss. The results in this study demonstrated citric acid treatment can effectively reduce the starch grain and soluble sugars content and improve mould resistance of bamboo, which can be attributed to the reduction of starch grain and soluble carbohydrates (such as glucose, fructose, and sucrose, etc.) in bamboo.

Color is one of the most important characteristics of a material’s appearance, which affects the additional value of bamboo and psychological feelings of users. Previous studies have shown that the dimensional stability, mildew resistance and durability of bamboo were improved after tung oil thermal treatment. In this study, the effects of tung oil thermal treatment on bamboo color at different temperatures and durations of time were investigated. The results show that the lightness (L*) of bamboo decreased as the tung oil temperature or duration of time increased. The red–green coordinates (a*) and color saturation (C*) of bamboo were gradually increased as the tung oil temperature rose from 23 °C to 160 °C, while the a* and C* were gradually decreased when the temperature continued to rise from 160 °C to 200 °C. There was no significant difference in the yellow–blue coordinates (b*) of bamboo when the duration was prolonged from 0.5 h to 3 h with tung oil thermal treatment at 140 °C. Eye movement data show that the popularity of bamboo furniture was significantly improved at 23–100 °C and slightly improved at 160–180 °C with tung oil treatment. Therefore, tung oil thermal treatment plays a positive role in improving visual effects and additional value of bamboo.

The effect of humidity and heat environmental conditions on the durability of conventional bamboo materials is a pressing issue in the reserving phase of biomass materials. In this study, the relationship between the main physicochemical, pyrolytic, and mechanical properties of bamboo before and after ageing has been investigated. Exposure of engineered bamboo raw materials with moisture content up to 10% to alternating humidity and heat cycles (20 °C 98% RH-30 °C 64% RH-40 °C 30% RH) of ageing (HHT) causes degradation of the chemical polymer matrix. Byk Gardner 6840 color difference meter, X-ray diffraction, Fourier transform infrared spectroscopy (FTIR), compression intensity, thermogravimetric-infrared spectroscopy (TG-IR), and density changes are used to assess the quality of the material before and after ageing. No significant changes in the moisture content within the range of 6.12 ± 0.327 after two weeks of the engineered bamboo during wet thermal cyclic ageing were determined. However, there were significant differences in mass loss (7.75–9.93 g), cellulose crystallinity, chemical changes, compression strength, and pyrolytic properties. Differences in specimen colors were observed during 10 weeks of the accelerated humidity heat cycling ageing, and TCD variations ranged from 3.75 to 20.08 and from 0.25 and 3.24, respectively. Reduced cellulose crystallinity (36.459–22.638%), axial compressive strength (63.07–88.09 MPa), and modulus of rupture (2409–4286 MPa) were found during aging, whereas deformation and ductility properties were improved. Both natural and humidity heat ageing improve thermal stability and peak pyrolysis rates (0.739–0.931; 0.731–0.797). Humidity heat cyclic ageing will assist in the design and risk assessment of warehousing environments for industrial applications.

Changes in bamboo composition and microstructure following 60Co gamma (γ) ray irradiation were investigated by solid state 13C cross-polarization (CP) magic-angle spinning (MAS) spectroscopic nuclear magnetic resonance spectrometry (NMR) and a field emission scanning electron microscope (FESEM). The results indicated that irradiation doses lower than 100 KGy resulted in the degradation of hemicelluloses via scission of molecular chains, but there was also repolymerization and condensation in lignin. Irradiation doses higher than 100 KGy resulted in the degradation of cellulose, hemicelluloses, and lignin by significant oxidation reaction and partial scission of biopolymer chains to yield more small fragments with carbonyl groups.

The helmet is a mandatory tool for safe production, and bamboo helmets can be used as an alternative to the traditional plastic safety helmet. In this study, bamboo helmets were modified with urea-formaldehyde resin and have shown excellent impact resistance, good color sensitivity, and high gloss. The excellent performance of the bamboo helmet comes from the structure designed by imitating the gradient characteristics of bamboo and the modification of urea-formaldehyde resin. The pores and defects of bamboo in the helmet modified by urea-formaldehyde resin are filled and repaired. The chemical combination of urea-formaldehyde resin and bamboo reduces bamboo’s crystallinity and improves the bamboo helmet’s impact resistance. The development of bamboo helmets provides a supplement and option for the traditional helmet market while opening up new ways of bamboo utilization.