Aluminum dross is a well-known industrial waste generated in the aluminium industry, and its recycling and reuse is still a worldwide issue. Herein, aluminum dross waste (ADW) was recycled to progressively replace the aggregate fraction of clay at 70, 75, 80, 85, and 90 wt% for the fabrication of Al₂O₃-SiO₂-rich porous castable refractories. Their physical properties and mechanical behavior were assessed by the measurement of linear shrinkage rate, bulk density, apparent porosity, cold crushing strength, and thermal conductivity. The microstructure and phase evolutions were analyzed via scanning electron microscopy (SEM) and X-ray diffraction (XRD). The incorporation of 85 wt% of ADW allowed the development of a waste-containing conventional refractory castable with improved properties as compared to those of the other samples. The sustainable refractory castable exhibited decent thermal conductivity and physical and mechanical characteristics, and is suitable for application as reheating furnace lining. It is a “green” practice to partially replace the traditional raw materials with industrial waste in the manufacture of conventional refractory castables and provides environmental and economic benefits.

Al₂O₃-bonded SiAlON ceramic with self-coating was prepared using aluminum dross and silicon solid waste as starting materials under ambient air conditions. The changes in phase, microstructure, and physical properties of the ceramic with temperature were analyzed and the formation mechanism of the SiAlON phase was elucidated. The results showed that higher temperature was more suitable for the preparation of SiAlON ceramics. As the temperature increased from 1400 to 1600 °C, the main phases in the ceramic transformed from mullite, Al₂O₃, and SiAlON to Al₂O₃ and SiAlON. An Al₂O₃-rich layer spontaneously coated the surface of the porous ceramic as Al melted and oxidized at high temperature. The thickness of this layer decreased as the temperature increased. The presence of Al₂O₃-rich coating layer impeded air flow, allowing nitriding of Si and Al, and the formation of the SiAlON phase in ambient air conditions. This study not only presents a strategy to successfully recycle aluminum dross and silicon solid waste but also offers a straightforward approach to preparing SiAlON material in air atmosphere.