Aluminum dross is a well-known industrial waste generated in the aluminium industry, and its recycling and reuse is still a worldwide issue. Herein, aluminum dross waste (ADW) was recycled to progressively replace the aggregate fraction of clay at 70, 75, 80, 85, and 90 wt% for the fabrication of Al₂O₃-SiO₂-rich porous castable refractories. Their physical properties and mechanical behavior were assessed by the measurement of linear shrinkage rate, bulk density, apparent porosity, cold crushing strength, and thermal conductivity. The microstructure and phase evolutions were analyzed via scanning electron microscopy (SEM) and X-ray diffraction (XRD). The incorporation of 85 wt% of ADW allowed the development of a waste-containing conventional refractory castable with improved properties as compared to those of the other samples. The sustainable refractory castable exhibited decent thermal conductivity and physical and mechanical characteristics, and is suitable for application as reheating furnace lining. It is a “green” practice to partially replace the traditional raw materials with industrial waste in the manufacture of conventional refractory castables and provides environmental and economic benefits.

Aluminum foam sandwich panels are excellent structure–function integrated materials. With high specific strength, cushioning energy absorption and sound absorption of aluminum foam material, they overcome the disadvantage of the low strength of single aluminum foam materials. In this paper, the response of aluminum sandwich panels comprising aluminum foam cores and carbon fiber reinforced plastic (CFRP) face-sheets was investigated under quasi-static three-point bending, and the effect of core thickness as well as core density on flexural loads and deformation modes was studied. The experimental results show that increasing the thickness and the density of the core materials can increase the flexural load and bending stiffness in the bending process. The aluminum foam sandwich panels mainly include the following deformation modes in the three-point bending process: indentation, core shear, face-sheet fracture and debonding.

This study utilizes desalted and denitrated treated aluminum dross (TAD) as a raw material, along with kaolin and 10 ppi (pores per inch) polyurethane foam as a template. The slurry is converted into an aluminum dross green body with a three-dimensional network structure using the impregnation method. A three-dimensional network aluminum dross ceramic framework (TAD_3D) is created at a sintering temperature of 1350 °C. The liquid 5A05 aluminum alloy at a temperature of 950 °C infiltrates into the voids of TAD_3D through pressureless infiltration, resulting in TAD_3D/5A05Al composite material with an interpenetrating phase composite (IPC) structure. The corrosion behavior of TAD_3D/5A05 composite material in sodium chloride solution was examined using the salt spray test (NSS) method. The study shows that the pores of the TAD3D framework, produced by sintering aluminum dross as raw material, are approximately 10 ppi. The bonding between TAD3D and 5A05Al interfaces is dense, with strong interfacial adhesion. The NSS corrosion time ranged from 24 h to 360 h, during which the composite material underwent pitting corrosion, crevice corrosion and self-healing processes. Results from Potentiodynamic Polarization (PDP) and Electrochemical Impedance Spectroscopy (EIS) indicate that, as corrosion progresses, the E_corr of TAD_3D/5A05Al decreases from −0.718 V to −0.786 V, and I_corr decreases from 0.398 μA·cm⁻² to 0.141 μA·cm⁻². A dense oxide film forms on the surface of the composite material, increasing the anodic Tafel slope and decreasing the cathodic Tafel slope, thus slowing down the rates of cathodic and anodic reactions. Factors such as lower interface corrosion resistance or a relatively weak passivation film at the interface do not significantly diminish the corrosion resistance of TAD_3D and 5A05Al. The corrosion resistance of the composite material initially decreases and then increases.

Biomass, as a clean energy source, has great potential in reducing emissions and protecting the environment. This study investigates the influence of biomass as a reducing agent on the magnetization roasting process of iron tailings, and utilizes methods such as TG, XRD, VSM to analyze the thermal decomposition of biomass, phase transition and magnetic transformation of iron tailings, in order to explain the mechanism of iron recovery through magnetization roasting. The results show that at a roasting temperature of 700 °C, roasting time of 15 min, and 10% of the poplar sawdust (PS) used, the iron grade of the concentrate obtained through weak magnetic separation is 65.2%, with iron recovery rate of 96%. The magnetic saturation intensity increases from 0.107 emu/g to 59.28 emu/g. The study demonstrates that the combination of biomass magnetization roasting and weak magnetic separation can effectively recover iron from low-grade iron tailings.