The present research article investigates the extraction of aluminum (Al) from an engineered CaO-Al₂O₃-SiO₂ slag by leaching with aqueous HCl under atmospheric pressure conditions. The slag is the by-product of an aluminothermic reduction process to produce metallurgical-grade silicon (Si) in a more sustainable way compared to conventional carbothermic reduction. One major challenge in the acidic leaching of aluminosilicate materials, like the slag treated in this study, is the possibility of SiO₂ gel formation during the leaching process. Extensive SiO₂ gel formation can make the separation of pregnant leach solution (PLS) from the leached residue impossible. Consequently, any acid leaching of aluminosilicate materials must be optimized for avoidance of these gelation phenomena. The present study first explores the leaching behavior of the calcium aluminosilicate slag in relation to the S/L ratio, with all other hydrometallurgical factors remaining stable (20.2% wt. HCl solution, 80 °C, optimized stirring rate), to determine at which value of this parameter SiO₂ gelation occurs. After determining the optimum S/L ratio for this system, an analysis of the behavior of Si in the PLS is presented, and the mechanism of SiO₂ gelation is explained based on critical assessment of these results against data provided from the scientific literature. It was found that the value of the pH of the PLS and the concentration of dissolved CaCl₂ and AlCl₃ are critical factors for the formation of filterable amorphous SiO₂. Under the optimum leaching conditions, PLS containing 37 g/L Al was obtained with concurrent avoidance of gelation phenomena.

Nano zero-valent iron (nZVI) is a well-known and effective remediation agent for various water contaminants. However, the challenges associated with its application, such as agglomeration and difficulty in recovery, have limited its effectiveness in large-scale treatment processes. In recent years, the development of nZVI nanocomposites has shown promise in addressing these challenges, as they offer improved stability, reactivity, and recoverability. This paper reviews the latest advancements in nZVI nanocomposites for water treatment and discusses their potential for the sustainable remediation of various contaminants, including heavy metals, organic contaminants, and emerging contaminants. The potential applications, limitations, and future prospects of nZVI nanocomposites in water treatment are discussed in detail. Overall, the findings suggest that nZVI nanocomposites have significant potential for sustainable water treatment and can contribute to the development of cost-effective and environmentally friendly water treatment solutions.

Scandium metal has generated a lot of interest during the past years. This is due to the various crucial applications it has found ground in and the lack of production in countries outside China and Russia. Apart from rare earth ores, scandium is present in a variety of wastes and by-products originating from metallurgical processes and is not currently being sufficiently valorised. One of these processes is the production of titanium dioxide, which leaves an acidic iron chloride solution with a considerably high concentration of scandium (10–140 ppm) and is currently sold as a by-product. This research aims to recover scandium without affecting the solution greatly so that it can still be resold as a by-product after the treatment. To achieve this, two commercial ion-exchange resins, VP OC 1026 and TP 260, are used in the column setup. Their breakthrough curves are plotted with mathematical modelling and compared. Results indicate that VP OC 1026 resin is the most promising for Sc extraction with a column capacity of 1.46 mg/mL, but Zr, Ti, and V coextract have high capacities, while Fe does not interfere with the adsorption.

Scandium, a valuable element with restricted production sources mainly situated in China and Russia, is typically obtained as a by-product during the production of various materials. As the demand for scandium grows in the expanding aluminum and fuel cell industries, and with significant investments in rare earth mining in the USA and Australia, there is a need to explore alternative recovery sources. This research investigates the recovery of scandium from an acid pregnant leaching solution using ion exchange resins. The pregnant leaching solution was obtained after the leaching of bauxite residue with sulfuric acid. Commercial resins with different functional groups were tested for their performance in scandium extraction. In addition, the co-adsorption of impurities, such as iron and titanium, was studied. The feed solution consisted of 12.7 mg/L Sc and main impurities of 272 mg/L Fe and 33.6 mg/L Ti and was pretreated before the ion exchange process by acidification with sulfuric acid and iron powder addition to suppress silica gel formation and minimize the Fe(III) content in the solution accordingly. Among the tested resins, a D₂EHPA-impregnated resin had high selectivity for Sc towards Ti, while a monophosphonic resin was also a promising option since it had a higher capacity for Sc but co-extracted Ti. These findings offer promising opportunities for the recovery of scandium from acid leaching solutions and could contribute to addressing the growing demand for this valuable element.

Calcium aluminate slag produced by the aluminothermic reduction of silica is tested as a candidate raw material for the hydrometallurgical production of pure aluminium chloride hexahydrate (ACH) through leaching with hydrochloric acid. The crystallization of ACH follows by sparging the pregnant liquor with hydrochloric gas. Almost total extraction of Al is achieved with the use of azeotropic HCl acid solution (5.9 M) at 80 °C and 1 h retention time. A pregnant liquor with approximately 20 wt% AlCl₃ is produced as a base for ACH crystallization by sparging it with gaseous HCl. The ACH produced is re-dissolved and crystallized three to four times until high purity is achieved. High purity ACH acts as a precursor for producing High Purity Alumina (HPA), a high added value material used in LEDs and lithium-ion batteries and other niche applications.