This review details the groundwork made in the most recent years on the development of TENGs for wave energy conversion systems and discusses future perspectives in the scope of autonomous, self-powered sensor buoys and other offshore floating platforms.

Due to its manufacturing and size tailoring ease, porous anodic alumina (PAA) templates are an elegant physical-chemical nanopatterning approach and an emergent alternative to more sophisticated and expensive methods currently used in nanofabrication. In this review, we will describe the ground work on the fabrication methods of PAA membranes and PAA-based nanostructures. We will present the specificities of the electrochemical growth processes of multifunctional nanomaterials with diversified shapes (e.g., nanowires and nanotubes), and the fabrication techniques used to grow ordered nanohole arrays. We will then focus on the fabrication, properties and applications of magnetic nanostructures grown on PAA and illustrate their dependence on internal (diameter, interpore distance, length, composition) and external (temperature and applied magnetic field intensity and direction) parameters. Finally, the most outstanding experimental findings on PAA-grown nanostructures and their trends for technological applications (sensors, energy harvesting, metamaterials, and biotechnology) will be addressed.

NiO nanoparticles (NPs) were prepared by a sol–gel process using the citrate route. The sol–gel parameters were tuned to obtain samples with different average particle sizes, ranging from 12 to 70 nm. Magnetic characterization revealed an increase in the blocking temperature with the diameter of the NPs and an increase in the effective magnetic anisotropy (K_eff) with decreasing particle size. The magnetic moment per particle was calculated for all samples using the susceptibility value at T = 300 K. The number of uncompensated spins per NP was found to be proportional to n^1/3 _S (n_S ≡ total number of spins), indicating that they are randomly distributed on the NP surface. For small diameters (<30 nm) the surface anisotropy constant was estimated, using, for NiO NPs, a recent model describing the evolution of K_eff with particle size. Hysteretic loops performed at low temperatures after field cooling displayed loop shifts (∼6.5 kOe in the field axis and ∼0.18 emu g⁻¹ vertically), coercive field enhancement (H_C ≈ 4.8 kOe) and training effects for the smaller NPs. The sample with NPs of larger diameters presented magnetic properties close to those of bulk NiO.