α-Pinene is the bicyclic, unsaturated terpene hydrocarbon present in many plants. Due to its beneficial chemical properties, this compound is of great interest and has found numerous applications as a raw material in many chemical industries as well as in medicine and cosmetics. The aim of this study was to evaluate the antioxidant activities of ethanolic extracts obtained from plants containing α-pinene and to test the properties of cosmetic emulsions prepared with these extracts. The raw plant materials consisted of fresh parts of Pinus sylvestris L., such as cones, needles, and branches, as well as dried unground and ground pinecones; dried and fresh Rosmarinus officinalis leaves; dried Levisticum officinale leaves; and dried Salvia officinalis L. leaves. The plant materials were individually extracted with 40% (v/v), 70% (v/v), and 96% (v/v) ethanol using ultrasound-assisted extraction (UAE) for 15, 30, or 60 min. This method is a green extraction technique, frequently applied to isolate active substances from plants. For the selected plant materials, Soxhlet extraction with 96% (v/v) ethanol was also performed. The qualitative and quantitative analyses of the components in the selected extracts were performed with gas chromatography coupled with mass spectrometry (GC-MS). The antioxidant activities of the extracts were evaluated with the DPPH and ABTS methods. The extracts of three plant materials with the highest antioxidant activities—dried Rosmarinus officinalis leaves, dried Salvia officinalis L. leaves, and dried and ground Pinus sylvestris L. cones—were selected to be incorporated in cosmetic emulsions containing glyceryl monostearate and Olivem 1000 as emulsifiers. The stabilities and antioxidant activities of the emulsions were evaluated. Moreover, the antimicrobial properties of the emulsions using microbiological tests were also determined. The findings suggest that the prepared emulsions are stable cosmetic products with a high antioxidant potential.

The work presents the results of studies on α-pinene oxidation over the TS-1 catalysts with different Ti content (in wt%): TS-1_1 (9.92), TS-1_2 (5.42), TS-1_3 (3.39) and TS-1_4 (3.08). No solvent was used in the oxidation studies, and molecular oxygen was used as the oxidizing agent. The effect of titanium content in the TS-1 catalyst, temperature, reaction time and amount of the catalyst in the reaction mixture on the conversion of α-pinene and the selectivities of appropriate products was investigated. It was found that it is most advantageous to carry out the process of α-pinene oxidation in the presence of the TS-1 catalyst with the titanium content of 5.42 wt% (TS-1_2), at the temperature of 85 °C, for 6 h and with the catalyst TS-1 content in the reaction mixture of 1 wt%. Under these conditions the conversion of α-pinene amounted to 34 mol%, and the selectivities of main products of α-pinene oxidation process were: α-pinene oxide (29 mol%), verbenol (15 mol%) and verbenone (12 mol%). In smaller quantities also campholenic aldehyde, trans-pinocarveol, myrtenal, myrtenol, L-carveol, carvone and 1,2-pinanediol were also formed. These products are of great practical importance in food, cosmetics, perfumery and medicine industries. Kinetic studies were also performed for the studied process.

In this work, we present the catalytic application of the naturally occurring zeolite, clinoptilolite, in the oxidation of α-pinene, a natural terpene compound. Clinoptilolites with different average particle sizes, designated as (in μm) clin_1 (20), clin_2 (50), clin_3 (200), and clin_4 (500–1000), were used as the green catalysts in the solvent-free oxidation of α-pinene with oxygen. Prior to their application in catalytic tests, the catalysts were characterized by the following methods: nitrogen sorption at 77 K, EDXRF, XRD, SEM, UV-Vis, and FTIR. The effects of the temperature, amount of the catalyst, and reaction time on the product’s selectivity and α-pinene conversion were determined. At the optimal conditions (a temperature of 100 °C, catalyst content (clin_4) in the reaction mixture of 0.05 wt%, and 210 min reaction time), the following compounds were obtained as the main products: α-pinene oxide (selectivity 29 mol%), verbenol (selectivity 17 mol%), and verbenone (selectivity 13 mol%). The conversion of α-pinene under these conditions amounted to 35 mol%. Additionally, the kinetic modeling of α-pinene oxidation over the most active catalyst (clin_4) was performed. The proposed method of oxidation is environmentally safe because it does not require the separation of products from the solvent. In addition, this method allows for managing the biomass in the form of turpentine, which is the main source of α-pinene. The catalytic application of clinoptilolite in the oxidation of α-pinene has not yet been reported in the literature.

In this work, carbon-supported nickel catalysts with different Ni content (1, 2.5, 5, 10, and 20 wt%) were tested in the oxidation of alpha-pinene in solvent-free reaction conditions. The process of catalyst preparation consisted of two stages. In the first stage, the activated carbon from spent coffee grounds was obtained. In the second stage, the active phase in the form of nickel compounds was applied using two methods: (1) the impregnation of the material with the nickel salt solution, and next reduction in H₂, and (2) the hydrothermal method in the autoclave using the reductor and the reaction stabilizer. The obtained catalysts were subjected to the following instrumental studies: FT-IR, XRD, SEM, and N₂ adsorption at −196 °C. The performed catalytic tests showed that the catalysts containing 5 wt% of Ni (porous material obtained by the impregnation method) and 1 wt% of Ni (porous material obtained by the hydrothermal method) were the most active in the oxidation of alpha-pinene, and the main oxidation products were alpha-pinene oxide, verbenol, and verbenone. Ultimately, the hydrothermal method of catalyst preparation turned out to be more advantageous because it allows one to obtain higher selectivities of the epoxide compound, probably due to the greater stability of this organic compound in pores.