Cost-effective activated carbons for CO₂ adsorption were developed from molasses using H₂SO₄, H₃PO₄, HCl, NaOH, and KOH as activating agents. At the temperature of 0 °C and a pressure of 1 bar, CO₂ adsorption equal to 5.18 mmol/g was achieved over activated carbon obtained by KOH activation. The excellent CO₂ adsorption of M-KOH can be attributed to its high microporosity. However, activated carbon prepared using HCl showed quite high CO₂ adsorption while having very low microporosity. The absence of acid species on the surface promotes CO₂ adsorption over M-HCl. The pore size ranges that are important for CO₂ adsorption at different temperatures were estimated. The higher the adsorption temperature, the more crucial smaller pores were. For 1 bar pressure and temperatures of 0, 10, 20, and 30 °C, the most important were pores equal and below: 0.733, 0.733, 0.679, and 0.536 nm, respectively.

This article describes the synthesis and characterization of porous carbon derived from waste banana peels by chemical activation with KOH or by activation KOH and urea modification. The as-synthesized samples were carefully characterized by various techniques. The prepared carbonaceous materials possess highly developed micropore and mesopore structures and high specific surface area (up to 2795 cm²/g for materials synthetized with KOH and 2718 cm²/g for activated carbons prepared with KOH and urea). A series of KOH-activated samples showed CO₂ adsorption at 1 bar to 5.75 mmol/g at 0 °C and 3.74 mmol/g at 25 °C. The incorporation of nitrogen into the carbon sorbent structure increased the carbon uptake capacity of the resulting materials at 1 bar to 6.28 mmol/g and to 3.86 mmol/g at 0 °C and 25 °C, respectively. It was demonstrated that treatment with urea leads to a significant increase in nitrogen content and, consequently, CO₂ adsorption, except for the material carbonized at 900 °C. At such a high temperature, almost complete decomposition of urea occurs. The results presented in this work could be used in the future for utilization of biomass such as banana peels as a low-cost adsorbent for CO₂ capture, which could have a positive impact on the environment and human health protection.

The effect of an alkali treatment (potassium hydroxide) on the properties of a commercial activated carbon has been studied. The aim of the treatment was to improve the adsorption properties of the material toward carbon dioxide. In the result of the treatment, silica contained in the raw carbon was removed and the density of the material increased. The changes in the surface chemistry were observed as well. The treatment of the activated carbon with KOH resulted in a complete removal of carboxy and lactone groups and a decrease of the general content of the acidic groups (more significant than that of basic groups). Simultaneously, the surface concentration of hydroxyl groups increased. The alkali treatment of activated carbon resulted in an increase of carbon dioxide uptake of 14% (measured using a volumetric method at 0℃). The adsorption of carbon dioxide on activated carbon has a mixed (physicochemical) character and that two types of adsorption sites are present at the surface. The adsorption energy varies roughly from 25 to 60 kJ/mol.