The present review addresses the latest findings and limitations in catalytic pyrolysis for the processing of plastic waste into valuable fuels. Compared to thermal degradation of plastics, catalytic pyrolysis provides better results in regards to the quality of the obtained liquid hydrocarbon fuel. Different types of catalysts can be used in order to improve the thermal degradation of plastics. Some of the most used catalysts are different types of zeolites (HUSY, HZSM-5, H$\beta$), Fluid Catalytic Cracking (FCC), silica-alumina catalysts, or natural clays. There is a need to find affordable and effective catalysts in the aim of achieving commercialization of catalytic pyrolysis of plastic waste. Therefore, this study summarizes and presents the most significant results found in the literature in regards to catalytic pyrolysis. This paper also investigates the symmetry effects of molecules on the pyrolysis process.

This paper presents the results of investigations on the pyrolysis of tyre waste in a laboratory fixed-bed batch reactor. The results regarding the influence of either the reaction temperature (425, 450, 475, and 500 °C) and the flow of the inert gas (0, 100, 300, and 500 mL/min) on product yield (referred to as pyrolysis of waste tyres) are also considered and discussed. On the basis of the abovementioned findings, the most appropriate experimental conditions were selected to contribute to a higher yield of pyrolysis oil. The sample of pyrolysis oil obtained from the experiments carried out in the selected optimal conditions (reaction time 120 min, temperature 450 °C and the inert gas flow of 100 mL/min) was subjected to calorimetric and infrared spectroscopy analysis.

Torrefaction is a thermochemical process, where biomass is obtained in temperature range from from 200 to 300 °C, in inert atmosphere with the aim to increase carbon content of biomass. In this paper, emphasis is on biomass feedstock types, different effects on torrefaction success, and torrefaction reactors.

This paper presents the results of investigations into the pyrolysis of waste polypropylene in a laboratory fixed-bed batch reactor. The experiments were designed and verified in such a way as to allow the application of the response surface methodology (RSM) in the development of an empirical mathematical model that quantifies the impacts mentioned above. The influence of the mass of the raw material (50, 100, and 150 g) together with the reactor temperature (450, 475, and 500 °C) and the reaction time (45, 50 and 75 min) was examined. It has been shown that the mass of the raw material, i.e., the filling volume of the reactor, has a significant influence on the pyrolysis oil yield. This influence exceeds the influence of reactor temperature and reaction time. This was explained by observing the temperature change inside the reactor at three different spots at the bottom, middle, and top of the reactor. The recorded temperature diagrams show that, with greater masses of feedstock, local overheating occurs in the middle part of the reactor, which leads to the overcracking of volatile products and, from there, to an increased formation of non-condensable gases, i.e., a reduced yield of pyrolytic oil.

Pyrolysis is a thermochemical process of degradation of organic compounds where the reaction takes place in an inert atmosphere. The process scale varies between industrial, semi-industrial or laboratory. During the pyrolysis process temperature has to be controlled, but, most of pyrolysis studies do not clearly state where the temperature is measured and weather the temperature field is uniform. In this paper thermal behavior of a laboratory scale fixed-bed reactor and energy consumption during pyrolysis processes were analyzed. Three different samples were used: mixture of plastic waste (sample 1), biomass (sample 2) and mixture of plastic waste and biomass (sample 3). The analysis of the thermal behavior of the reactor indicates that with careful regulation or temperature control of the process, one can obtain diagrams that can be used for the purpose of recording thermally intensive processes, similar to more complex thermogravimetric (TG) and derivative thermogravimetric (DTG) analyses. It has been shown that it is possible to change the heating rate and the overall energy efficiency of the process by simply choosing the appropriate raw material mixture.

This paper presents the results of investigations into the pyrolysis of waste polypropylene in a laboratory fixed-bed batch reactor. The experiments were designed and verified in such a way as to allow the application of the Response Surface Methodology (RSM) in the development of an empirical mathematical model that quantifies the impacts mentioned above. The influence of the mass of the raw material (50, 100 and 150 g), together with the reactor temperature (450, 475 and 500 °C) and the reaction time (45, 50 and 75 min) was examined. It has been shown that the mass of the raw material, i.e. the filling volume of the reactor, has a significant influence on the pyrolysis oil yield. This influence exceeds the influence of reactor temperature and reaction time. This was explained by observing the temperature change inside the reactor at three different spots at the bottom, middle and top of the reactor. Recorded temperature diagrams show that with greater masses of feedstock, local overheating occurs in the middle part of the reactor, which leads to overcracking of vapor products, and from there to an increased formation of non-condensable gases, i.e. reduced yield of pyrolytic oil.