Changes in composition, crystal structure and phase transformations of B2-(Ni,Pt)Al coatings upon isothermal oxidation experiments (natural and scale free oxidation) at 1100 °C, as a function of time beyond their martensitic transformation, are reported. Specifically, the analysis of lattice parameter and composition are performed to identify changes in the B2-(Ni,Pt)Al phase upon the chemically-driven L1₀-(Ni,Pt)Al and L1₂-(Ni,Pt)₃Al transformations. The B2-(Ni,Pt)Al phase was found to disorder and transform the martensite during the heat treatments for both oxidation experiments at approximately 36.3 and 40.9 at. % of Al, 47.7 and 42.9 at. % of Ni, 6.2 and 8.5 at. % of Pt, 4.2 and 2.9 at. % of Cr and 4.4 and 3.8 at. % of Co. The lattice constant and the long-range order parameter of the B2-(Ni,Pt)Al phase decreased linearly as a function of the elemental content irrespective of the nature of the oxidation experiments.