Nosocomial infections, a prevalent issue in intensive care units due to antibiotic overuse, could potentially be addressed by metal oxide nanoparticles (NPs). However, there is still no comprehensive understanding of the impact of NPs’ size on their antibacterial efficacy. Therefore, this study provides a novel investigation into the impact of ZnO NPs’ size on bacterial growth kinetics. NPs were synthesized using a sol–gel process with monoethanolamine (MEA) and water. X-ray diffraction (XRD), transmission electron microscopy (TEM), and Raman spectroscopy confirmed their crystallization and size variations. ZnO NPs of 22, 35, and 66 nm were tested against the most common nosocomial bacteria: Escherichia coli, Pseudomonas aeruginosa (Gram-negative), and Staphylococcus aureus (Gram-positive). Evaluation of minimum inhibitory and bactericidal concentrations (MIC and MBC) revealed superior antibacterial activity in small NPs. Bacterial growth kinetics were monitored using optical absorbance, showing a reduced specific growth rate, a prolonged latency period, and an increased inhibition percentage with small NPs, indicating a slowdown in bacterial growth. Pseudomonas aeruginosa showed the lowest sensitivity to ZnO NPs, attributed to its resistance to environmental stress. Moreover, the antibacterial efficacy of paint containing 1 wt% of 22 nm ZnO NPs was evaluated, and showed activity against E. coli and S. aureus.

V-TiO₂ photocatalyst with 0 ≤ V ≤ 20 mol% was prepared via the sol–gel method based on mixed oxide titanium–vanadium nanoparticles with size and composition control. The mixed oxide vanadium–titanium oxo-alkoxy nanonoparticles were generated in a chemical micromixing reactor, coated on glass beads via liquid colloid deposition method and underwent to an appropriate thermal treatment forming crystallized nanocoatings. X-ray diffraction, Raman, thermogravimetric and differential thermal analyses confirmed anatase crystalline structure at vanadium content ≤ 10 mol%, with the cell parameters identical to those of pure TiO₂. At a higher vanadium content of ~20 mol%, the material segregation began and orthorhombic phase of V₂O₅ appeared. The crystallization onset temperature of V-TiO₂ smoothly changed with an increase in vanadium content. The best photocatalytic performance towards methylene blue decomposition in aqueous solutions under UVA and visible light illuminations was observed in V-TiO₂ nanocoatings with, respectively, 2 mol% and 10 mol% vanadium.

Well-crystallized ZnMn ₂ O ₄ thin films were fabricated via a facile single-step plasma process without calcination. These films showed excellent electrochemical performance and remarkable stability as cathode materials for zinc-ion batteries (ZIBs).

Cu–TiO₂ nanoparticles of a broad range of compositions with 0, 0.002, 0.005, 0.02, 0.05, 0.2, 0.5, 1.0, 2.0, 3.0, 5.0, 7.0 and 10.0 mol% Cu were synthesized via the sol–gel method using copper (II) acetate and titanium tetraisopropoxide (TTIP) precursors at a low hydrolysis ratio of H = 1.25, which favours homogeneous TiO₂ nucleation and Cu dispersion in the host matrix at nanoscale. The precipitated materials were dried at 80 °C and calcined at 450, 500, and 550 °C to form crystalline nanopowders, whose photocatalytic activity was evaluated on the decomposition of a representative pollutant, methylene blue (MB), in aqueous solutions under UVA and sunlight illuminations. The compositions with small Cu content of ~0.05 mol% showed the highest activity. A gain of activity over pure titania of 4 times after calcination at 450 °C, 2.5 times at 500 °C and 20% at 550 °C was measured under UVA illumination. Even higher gain of activity observed under sunlight illumination might be due to an extension of action spectrum to the visible range due to intra-gap defect states produced by Cu²⁺ insertion. The time-resolved microwave conductivity (TRMC) measurements of the photoinduced charges relaxation suggest that both excessive calcination temperature and Cu content decrease the activity due to Cu-defects clustering. Modelling relates the activity to the photoinduced electron-hole pair separation; the optimal Cu content is explained by accessibility of the recombination centre by a conduction band (CB) electron. Accordingly, an increase in calcination temperature resulted in a longer pathlength of CB electron.