Efficient water electrolysis is one of the key issues in realizing a clean and renewable energy society based on hydrogen fuel. However, several obstacles remain to be solved for electrochemical water splitting catalysts, which are the high cost of noble metals and the high overpotential of alternative catalysts. Herein, we suggest Ni-based alternative catalysts that have comparable performances with precious metal-based catalysts and could be applied to both cathode and anode by precise phase control of the pristine catalyst. A facile microwave-assisted procedure was used for NiO nanoparticles anchored on reduced graphene oxide (NiO NPs/rGO) with uniform size distribution in ~1.8 nm. Subsequently, the Ni-NiO dual phase of the NPs (A-NiO NPs/rGO) could be obtained via tailored partial reduction of the NiO NPs/rGO. Moreover, we demonstrate from systematic HADDF-EDS and XPS analyses that metallic Ni could be formed in a local area of the NiO NP after the reductive annealing procedure. Indeed, the synergistic catalytic performance of the Ni-NiO phase of the A-NiO NPs/rGO promoted hydrogen evolution reaction activity with an overpotential as 201 mV at 10 mA cm⁻², whereas the NiO NPs/rGO showed 353 mV. Meanwhile, the NiO NPs/rGO exhibited the most excellent oxygen evolution reaction performance among all of the Ni-based catalysts, with an overpotential of 369 mV at 10 mA cm⁻², indicating that they could be selectively utilized in the overall water splitting. Furthermore, both catalysts retained their activities over 12 h with constant voltage and 1000 cycles under cyclic redox reaction, proving their high durability. Finally, the full cell capability for the overall water electrolysis system was confirmed by observing the generation of hydrogen and oxygen on the surface of the cathode and anode.

We present the dual phase photocatalysts enabling 3-fold longer charge carrier lifetime and 3-fold enhanced photocatalytic water oxidation by integrating a tetragonal zircon-type BiVO ₄ as an electron mediator for Z -scheme charge transfer.

Here, we report on the formation of homogeneous nanostructures and the thermal properties of quaternary system with AgPb _m SbTe _m+2 ( m = 18) that were synthesized via nanostructure crystallization engineering.

An accurate humidity measurement is essential in various industries, including product stability, pharmaceutical and food preservation, environmental control, and precise humidity management in experiments and industrial processes. Crafting effective humidity sensors through precise material selection is crucial for detecting minute humidity levels across various fields, ultimately enhancing productivity and maintaining product quality. Metal–organic frameworks (MOFs), particularly zeolitic imidazolate frameworks (ZIFs), exhibit remarkable properties and offer a wide range of applications in catalysis, sensing, and gas storage due to their structural stability, which resembles zeolites. The previous research on MOF-based humidity sensors have primarily used electrical resistance-based methods. Recently, however, interest has shifted to capacitive-based sensors using MOFs due to the need for humidity sensors at low humidity and the resulting high sensitivity. Nevertheless, further studies are required to optimize particle structure and size. This study analyzes ZIF-8, a stable MOF synthesized in varying particle sizes, to evaluate its performance as a humidity sensor. The structural, chemical, and sensing properties of synthesized ZIF-8 particles ranging from 50 to 200 nanometers were examined through electron microscopy, spectroscopic, and electrochemical analyses. The fabricated copper electrodes combined with these particles demonstrated stable and linear humidity sensing capabilities within the range of 3% to 30% relative humidity (RH).