The thermal stability of natural fiber composites is a relevant aspect to be considered since the processing temperature plays a critical role in the manufacturing process of composites. At higher temperatures, the natural fiber components (cellulose, hemicellulose, and lignin) start to degrade and their major properties (mechanical and thermal) change. Different methods are used in the literature to determine the thermal properties of natural fiber composites as well as to help to understand and determine their suitability for a certain applications (e.g., Thermogravimetric analysis (TGA), differential scanning calorimetry (DSC), and differential mechanical thermal analysis (DMA)). Weight loss percentage, the degradation temperature, glass transition temperature (T_g), and viscoelastic properties (storage modulus, loss modulus, and the damping factor) are the most common thermal properties determined by these methods. This paper provides an overview of the recent advances made regarding the thermal properties of natural and hybrid fiber composites in thermoset and thermoplastic polymeric matrices. First, the main factors that affect the thermal properties of natural and hybrid fiber composites (fiber and matrix type, the presence of fillers, fiber content and orientation, the treatment of the fibers, and manufacturing process) are briefly presented. Further, the methods used to determine the thermal properties of natural and hybrid composites are discussed. It is concluded that thermal analysis can provide useful information for the development of new materials and the optimization of the selection process of these materials for new applications. It is crucial to ensure that the natural fibers used in the composites can withstand the heat required during the fabrication process and retain their characteristics in service.

The main objective of this work was to investigate the effect of hybridization on the mechanical and thermal properties of intralaminar natural fiber-reinforced hybrid composites based on sisal. Ramie, sisal and curauá fibers were selected as natural fiber reinforcements for the epoxy matrix based composites, which were produced by the hand lay-up technique. Tensile, flexural and impact tests were carried out according to American society for testing and materials (ASTM) standards to characterize the hybrid composites, while differential scanning calorimetry (DSC) and thermogravimetric analysis (TGA) were used to evaluate the thermal properties. It was found that the mechanical properties are improved by hybridization of sisal based composites. The thermal analysis showed that the hybridization did not significantly affect the thermal stability of the composites. A scanning electron microscopy (SEM) was used to examine the fracture surface of the tested specimens. The SEM images showed a brittle fracture of the matrix and fiber breakage near the matrix.

The increase in the use of additive manufacturing (AM) has led to the need for filaments with specific and functional properties in face of requirements of structural parts production. The use of eco-friendly reinforcements (i.e., natural fibers) as an alternative to those more traditional synthetic counterparts is still scarce and requires further investigation. The main objective of this work was to develop short curauá fiber-reinforced polylactic acid (PLA) composites made via fused deposition modeling. Three different fiber lengths (3, 6, and 8 mm), and three concentrations in terms of weight percentage (2, 3.5, and 5 wt.%) were used to fabricate reinforced PLA filaments. Tensile and flexural tests in accordance with their respective American Society for Testing and Materials (ASTM) standards were performed. A thermal analysis was also carried out in order to investigate the thermal stability of the new materials. It was found that the main driving factor for the variation in mechanical properties was the fiber weight fraction. The increase in fiber length did not provide any significant benefit on the mechanical properties of the curauá fiber-reinforced PLA composite printed parts. The composites produced with PLA filaments reinforced by 3 mm 2% curauá fiber presented the overall best mechanical and thermal properties of all studied groups. The curauá fiber-reinforced PLA composites made via fused deposition modeling may be a promising innovation to improve the performance of these materials, which might enable them to serve for new applications.

In this paper, the effect of a novel fibre reinforcement architecture in the adhesively bonded joint efficiency of natural fibre reinforced composites (NFRC) was investigated. Two different reinforcement techniques were used: intralaminar reinforcement (2D) and orthogonal-through-the-thickness reinforcement (3D). The aim of the novel architecture is to enhance the transverse properties of the adherend (transverse strength and fracture toughness) in order to delay or avoid delamination failures. A jute bidirectional fabric was used as a base primary reinforcement phase and curauá, sisal, ramie, hemp and glass fibres were used as secondary reinforcement phases for the 2D and 3D fibre reinforcement architectures. Single lap joints (SLJs) bonded with an epoxy adhesive used in the automotive industry were fabricated with these adherends and the efficiency of the joints was investigated by comparing them to glass (GFRP) and carbon (CFRP) pure synthetic fibre reinforced composite joints. It was found that the novel architecture was successful in reaching the failure load of the synthetic composite joints for SISAL 3D, CURAUÁ 2D and CURAUÁ 3D SLJs. Therefore, NFRC bonded joints can be a viable replacement for synthetic fibre composite joints at no load-bearing loss.

The main objective of this research centered on investigating the effect of the addition of multi-walled carbon nanotubes (MWCNTs) on the mechanical and thermal properties of curauá-fiber-reinforced composites. The MWCNTs were added either to the fiber surface or into the resin matrix as the second reinforcing phase. The MWCNT-modified curauá fibers as well as raw fibers were characterized using a single-fiber tensile test, TGA, and FTIR analysis. Further, different composite samples, namely, pure curauá, (curauá + MWCNTs) + resin and curauá+ (resin + MWCNTs), were manufactured via compression molding and tested to determine their mechanical and thermal properties. Scanning electron microscopy (SEM) analysis was used to examine the surfaces of the tested fibers. It was found that the addition of MWCNTs to the curauá fibers resulted in positive effects (an enhancement in properties was found for the MWCNT-modified fibers and their composites). The addition of MWCNTs also increased the thermal stability of the natural fibers and composites.