Commercial grade sulfonated-Polyethersulfone (S-PES) and functionalized multiwall carbon nanotube (f-MWCNT)/polyvinylpyrrolidone (PVP) nanocomposites (NCs) were used to enhance and optimize the antifouling, protein resistance and protein separation properties of the S-PES ultrafiltration membranes. The polarities of sulfonic groups of S-PES, carbonyl carbon of pyrrolidone, hydroxyl and carboxyl groups of f-MWCNT in the membrane composition helped to strongly bind each other through hydrogen bonding, as shown by Fourier-transform infrared spectroscopy (FTIR). These binding forces greatly reduced the leaching of NCs and developed long finger-like projection, as confirmed by elution ratio and cross-sectional studies of the membranes via field emission scanning electron microscope (FESEM). The contact angle was reduced up to 48% more than pristine PES. Atomic force microscopy (AFM) was employed to study the various parameters of surface roughness with 3d diagrams, while grain analysis of membrane surface provided a quantitative estimation about volume, area, perimeter, length, radius and diameter. The NCs/S-PES enhanced the flux rate with an impressive (80–84%) flux recovery ratio and (58–62%) reversible resistance (R_r) value in situ, with 60% and 54.4% lesser dynamic and static protein adsorption. The best performing membrane were reported to remove 31.8%, 66.3%, 83.6% and 99.9% for lysozyme-(14.6 kDa), trypsin-(20 kDa), pepsin-(34.6 kDa) and bovine serum albumin (BSA-66 kDa), respectively.

This study investigated the influence of dope extrusion rate (DER) and post-treatment effect on the morphology, permeation, and metal ion rejection by polyethersulfone/lithium bromide (PES/LiBr)-based hollow fiber (HF) membranes. HF fibers were spun with 2.25, 2.5, and 3.1 ratios of DER to bore fluid rate (BFR), wherein DER varied from 11.35, 12.5, to 15.6 mL/min with a fixed BFR (5 mL/min). Molecular weight cutoff (MWCO), pore size, water flux, and flux recovery ratio were determined, whereas lake water was used to observe the rejection rate of dissolved metallic ions. Results showed that with the increase of the DER wall thickness (WT), HFs increased from 401.5 to 419.5 um, and furthermore by the post-treatments up to 548.2 um, as confirmed by field emission scanning electron microscope (FESEM) analysis. Moreover, MWCO, pore size, and the pure water permeation (PWP) of the HF membranes decreased, while the separation performance for polyethylene glycol (PEG) solute increased with increasing DER. Post-treated HFs from 11.35 mL/min of DER showed 93.8% of MWCO value with up to 90% and 70% rejection of the arsenic and chromium metallic ions, respectively, in comparison with all other formulated HFs.

A wide range of synthetic polymers is employed in hemodialysis (HD) applications, each offering unique advantages and potential limitations that can impact patient outcomes. These polymers are primarily chosen for their excellent permeability to uremic solutes and superior biocompatibility, which are critical for efficient blood purification. However, challenges such as membrane fouling, protein adsorption and long-term blood compatibility remain concerns that can affect the overall efficacy and safety of the treatment. In recent years, advances in polymer engineering have led to the development of new membrane materials with improved selectivity, durability, and reduced inflammatory response. Polysulfone (PS), polyurethane (PU), polyethersulfone (PES) and polyacrylonitrile (PAN) are among the most widely used polymers in commercial dialyzers, each with specific performance characteristics tailored to patient needs. In the current review, we overviewed various types of polymers used as hemodialyzer material and their contribution to enhance patient life span.