Pterocarpus santalinus and Pterocarpus tincorius are commonly used traded timber species of the genus Pterocarpus. P. santalinus has been listed in Appendix II of the Convention on International Trade in Endangered Species of Wild Fauna and Flora (CITES). As a non-CITES species, P. tincorius is also indiscriminately labeled as P. santalinus due to the similar macroscopic and microscopic features with P. santalinus. In order to understand the molecular discrimination between these easily confused species, xylarium heartwoods of these two species were extracted by three different kinds of solvents and analyzed using gas chromatography–mass spectrometry (GC-MS). Multivariate analyses were also applied for the selection of marker compounds that are distinctive between P. santalinus and P. tincorius. A total of twenty volatile compounds were detected and tentatively identified in three kinds of extracts, and these compounds included alcohols, stilbenoids, esters, aromatic hydrocarbons, ketones, miscellaneous, phenols, and flavonoids. GC-MS analyses also revealed that extraction solvents including ethanol and water (EW), ethyl acetate (EA), and benzene–ethanol (BE) gave the best chemotaxonomical discrimination in the chemical components and relative contents of the two Pterocarpus species. After chemometric analyses, EW displayed higher predictive accuracy (100%) than those of EA extract (83.33%) and BE extract (83.33%). Furthermore, spathulenol (17.58 min) and pterostilbene (23.65 min) were elucidated as the critical compounds for the separation of the EW extracts of P. santalinus and P. tinctorius. Thus, a protocol of GC-MS and multivariate analyses was developed to use for successfully distinguishing P. santalinus from P. tinctorius.

Bamboo is a natural fibre reinforced composite with excellent performance which is, to a certain extent, an alternative to the shortage of wood resources. The heterogeneous distribution and molecular structure of lignin is one of the factors that determines its performance, and it is the key and most difficult component in the basic research into the chemistry of bamboo and in bamboo processing and utilization. In this study, the distribution of lignin components and lignin content in micro-morphological regions were measured in semi-quantitative level by age and radial location by means of visible-light microspectrophotometry (VLMS) coupled with the Wiesner and Maule reaction. There as guaiacyl lignin and syringyl lignin in the cell wall of the fibre. Lignin content of the secondary cell wall and cell corner increased at about 10 days, reached a maximum at 1 year, and then decreased gradually. From 17 days to 4 years, the lignin content of the secondary cell wall in the outer part of bamboo is higher than that in the middle part (which is, in turn, higher than that in the inner part of the bamboo). VLSM results of the micro-morphological regions showed that bamboo lignification developed by aging. Guaiacyl and syringl lignin units can be found in the cell wall of the fibre, parenchyma, and vessel. There was a difference in lignin content among different ages, different radial location, and different micro-morphological regions of the cell wall. The fibre walls were rich in guaiacyl lignin in the early stage of lignification and rich in syringyl units in the later stage of lignification. The guaiacyl and syringyl lignin deposition of bamboo green was earlier than that of the middle part of bamboo culm, and that of the middle part of bamboo culm was earlier than that of bamboo yellow. The single molecule lignin content of the thin layer is higher than that of thick layers, while the primary wall is higher than the secondary cell wall, showing that lignin deposition is consistent with the rules of cell wall formation. The obtained cytological information is helpful to understand the origin of the anisotropic, physical, mechanical, chemical, and machining properties of bamboo.