Structural and chemical deterioration and its impact on cell wall mechanics were investigated for visually intact cell walls (VICWs) in waterlogged archaeological wood (WAW). Cell wall mechanical properties were examined by nanoindentation without prior embedding. WAW showed more than 25% decrease of both hardness and elastic modulus. Changes of cell wall composition, cellulose crystallite structure and porosity were investigated by ATR-FTIR imaging, Raman imaging, wet chemistry, ¹³C-solid state NMR, pyrolysis-GC/MS, wide angle X-ray scattering, and N₂ nitrogen adsorption. VICWs in WAW possessed a cleavage of carboxyl in side chains of xylan, a serious loss of polysaccharides, and a partial breakage of β-O-4 interlinks in lignin. This was accompanied by a higher amount of mesopores in cell walls. Even VICWs in WAW were severely deteriorated at the nanoscale with impact on mechanics, which has strong implications for the conservation of archaeological shipwrecks.

Waterlogged archaeological wood (WAW) artifacts, made of natural biodegradable polymers, are important parts of many precious cultural heritages. It is of great importance to understand the hygroscopic behavior of WAW in different deterioration states for the development of optimal drying processes and choices of safe storage in varying conditions. This was investigated in a case-study using two Hopea (Giam) and two Tectona (Teak) WAW samples collected from the Xiaobaijiao No.1 shipwreck. The deterioration state of WAW was evaluated by the maximum water content (MWC) method and by the cell morphological structure. Both Hopea and Tectona WAW could be classified into moderately and less decayed WAW. The hygroscopic behavior of moderately and less decayed WAW was then comparatively investigated using Dynamic Vapor Sorption (DVS) measurements alongside two sorption fitting models. Compositional analysis and hydroxyl accessibility measurements of WAW cell walls were shown to correlate with the hygroscopicity of WAW in different deterioration states. It was concluded that moderately decayed WAW possessed higher hygroscopicity and hysteresis than less decayed WAW because of the lower relative content of polysaccharides and the higher relative content of lignin, including the slow hydrolysis of O-acetyl groups of xylan and the partial breakage of β-O-4 interlinks, accompanied by an increased hydroxyl accessibility. This work helps in deciding on which consolidation measures are advised for shipwreck restauration, i.e., pretreatments with specific consolidates during wood drying, particularly for wooden artifacts displayed in museums.

Pterocarpus santalinus and Pterocarpus tincorius are commonly used traded timber species of the genus Pterocarpus. P. santalinus has been listed in Appendix II of the Convention on International Trade in Endangered Species of Wild Fauna and Flora (CITES). As a non-CITES species, P. tincorius is also indiscriminately labeled as P. santalinus due to the similar macroscopic and microscopic features with P. santalinus. In order to understand the molecular discrimination between these easily confused species, xylarium heartwoods of these two species were extracted by three different kinds of solvents and analyzed using gas chromatography–mass spectrometry (GC-MS). Multivariate analyses were also applied for the selection of marker compounds that are distinctive between P. santalinus and P. tincorius. A total of twenty volatile compounds were detected and tentatively identified in three kinds of extracts, and these compounds included alcohols, stilbenoids, esters, aromatic hydrocarbons, ketones, miscellaneous, phenols, and flavonoids. GC-MS analyses also revealed that extraction solvents including ethanol and water (EW), ethyl acetate (EA), and benzene–ethanol (BE) gave the best chemotaxonomical discrimination in the chemical components and relative contents of the two Pterocarpus species. After chemometric analyses, EW displayed higher predictive accuracy (100%) than those of EA extract (83.33%) and BE extract (83.33%). Furthermore, spathulenol (17.58 min) and pterostilbene (23.65 min) were elucidated as the critical compounds for the separation of the EW extracts of P. santalinus and P. tinctorius. Thus, a protocol of GC-MS and multivariate analyses was developed to use for successfully distinguishing P. santalinus from P. tinctorius.

Pterocarpus santalinus, listed in CITES Appendix II, is an endangered timber species as a result of illegal harvesting due to its high value and commercial demand. The growing demand for P. santalinus and timbers with the morphologically similar Pterocarpus tinctorius has resulted in confusion as well as identification problems. Therefore, it is of vital importance to explore reliable ways to accurately discriminate between P. santalinus and P. tinctorius. In this study, the method of direct analysis in real time and fourier transform ion cyclotron resonance mass spectrometry (DART-FTICR-MS), combined with multivariate statistical analysis, was used to extract chemical information from xylarium wood specimens and to explore the feasibility of distinguishing these two species. Significant differences were observed in their DART-FTICR-MS spectra. Orthogonal partial least square-discriminant analysis (OPLS-DA) showed the highest prediction, with an accuracy of 100%. These findings demonstrate the feasibility of authenticating wood types using DART-FTICR-MS coupled with multivariate statistical analysis.