High-density polyethylene (HDPE) pipes are the preferred pipes of water systems in nuclear power plants because they are durable, corrosion-free, easy to install, and not subject to fouling. However, their long-term performance can be affected by welding defects. In this paper, the effect of welding defects on the long-term performance of HDPE pipe butt fusion joints was studied using a creep test. A welding defect with a hole or inclusion in the joint was simulated by artificially inserting a copper ball during butt fusion welding. The test results showed that the creep life of the joint decreased with increased defect size. An expression describing the creep life and the defect ratio was obtained according to the test results. In addition, the test results showed that the creep life of the joint without a welding bead was about 50% of that in a joint with a welding bead.

The utilization of high-density polyethylene (HDPE) pipes is prevalent in water transportation due to their exceptional durability, resistance to corrosion, and ease of installation. Traditionally, butt fusion welding has been employed to connect HDPE pipes. In this study, scanning electron microscopy (SEM) was utilized to examine the microstructure of butt fusion welded joints of HDPE pipes, while the stepped isostress method (SSM) was employed to investigate their creep behavior at 100 °C in ambient air. SEM results revealed a significant presence of craze or lamellae in the base material, whereas minimal occurrences of craze or lamellae were observed in the melt zone. The results obtained from the SSM indicated that the creep life of butt fusion welded joints of HDPE pipes was not adversely affected by the welding bead, and their creep life was no less than that of the base material when ductile creep failure occurred.