Superhydrophilic coatings have been widely used for the surface modification of membranes or biomedical devices owing to their excellent antifouling properties. However, simplifying the modification processes of such materials remains challenging. In this study, we developed a simple and rapid one-step co-deposition process using an oxidant trigger to fabricate superhydrophilic surfaces based on dopamine chemistry with sulfobetaine methacrylate (SBMA). We studied the effect of different oxidants and SBMA concentrations on surface modification in detail using UV–VIS spectrophotometry, dynamic light scattering, atomic force microscopy, X-ray photoelectron spectroscopy, and surface plasmon resonance. We found that NaIO₄ could trigger the rate of polymerization and the optimum ratio of dopamine to SBMA is 1:25 by weight. This makes the surface superhydrophilic (water contact angle < 10°) and antifouling. The superhydrophilic coating, when introduced to polyester membranes, showed great potential for oil/water separation. Our study provides a complete description of the simple and fast preparation of superhydrophilic coatings for surface modification based on mussel-inspired chemistry.

The magnetic properties of the new Fe₄₁Ni₂₈Co₁₇Al_11.5(Ti+Nb)_2.5 (at. %) shape memory alloy system were studied in this work. The magnetic properties were characterized by thermo-magnetization and a vibrating sample magnetometer (VSM). In iron-based shape memory alloys, aging heat treatment is crucial for obtaining the properties of superelasticity and shape memory. In this study, we focus on the magnetization, martensitic transformation temperatures, and microstructure of this alloy during the aging process at 600 °C. From the X-ray diffraction (XRD) results, the new peak γ’ is presented during the aging process. The intensity of this new peak (γ’) increases with the aging time, while the intensity of the FCC (111) austenite peak decreases with aging time. Transmission electron microscope (TEM) results show that the size of the precipitate increases with increasing the aging times from 24 to 72 h. Thermo-magnetization results show that: (1) phase transformation is observed when the aging time is at least 24 h, (2) the transformation temperature increases with the aging time, (3) transformation temperatures tend to increase while the magnetic field increases from 0.05 to 7 Tesla, and (4) the magnetization saturates after aging time reaches 24 h. Vibrating sample magnetometer (VSM) results show that thermal process was found to significantly affect the magnetic properties of this alloy, especially on saturated magnetic magnetization and magnetic moment reversal behavior.