The effect of natural aging on the stress corrosion cracking (SCC) of A201-T7 alloy was investigated by the slow strain rate testing (SSRT), transmission electron microscopy (TEM), scanning electron microscopy (SEM), differential scanning calorimetry (DSC), conductivity, and polarization testing. The results indicated that natural aging could significantly improve the resistance of the alloys to SCC. The ductility loss rate of the unaged alloy was 28%, while the rates for the 24 h and 96 h aged alloys were both 5%. The conductivity of the as-quenched alloy was 30.54 (%IACS), and the conductivity of the 24 h and 96 h aged alloys were decreased to 28.85 and 28.65. After T7 tempering, the conductivity of the unaged, 24 h, and 96 h aged alloys were increased to 32.54 (%IACS), 32.52 and 32.45. Besides, the enthalpy change of the 24 h and 96 h aged alloys increased by 36% and 37% compared to the unaged alloy. The clustering of the solute atoms would evidently be enhanced with the increasing time of natural aging. Natural aging after quenching is essential to improve the alloy’s resistance to SCC. It might be due to the prevention of the formation of the precipitation free zone (PFZ) after T7 tempering.

The results of studies on the corrosion protectiveness and thermal conductivity of reduced graphene oxide–BaSO₄ epoxy composites are reported here. A commercial epoxy resin and reduced graphene oxide (rGO) were blended with a hardening reagent and then mixed with prepared BaSO₄–epoxy resin (B–epoxy). The reduced graphene oxide–BaSO₄–epoxy composite (rGO–B–epoxy) paste was used to coat the surfaces of Al 7205 alloy and the corrosion and thermal properties were investigated. A corrosion test in a 3.5 wt% synthetic sea water solution showed that the composite coating containing BaSO₄ had the best corrosion resistance. Moreover, the rGO–B–epoxy composite showed better protection against corrosion than the epoxy alone. The rGO–B–epoxy composite with 5 wt% BaSO₄ had an in-plane coefficient of thermal conductivity of approximately 165.0 W/m K, and the in-plane thermal diffusivity was 71.38 mm²/s. In standard thermal conductivity tests, all three samples had values below 40 W/m K. The rGO–B–epoxy composites showed good surface corrosion protection and in-plane thermal conductivity.