Despite recent advances in bonding restorations, which are the basis of restorative dentistry, secondary caries are still able to form. Previously, a novel fluoride-containing zinc and copper (ZCF) nanocomposite was introduced to prevent the formation of caries due to its antibacterial activity. In this study, we studied the impact of ZCF nanoparticles on the adhesive strength of bonding restorations through micro-tensile bond strength (µTBS) testing. The impact of antibacterial and matrix metalloproteinase (MMP) inhibitors on the nanoparticles was also examined. The nanocomposites were prepared using a simple one-step homogeneous co-precipitation method at a low temperature. A self-etch adhesive was applied to 10 extracted caries-free human molars with (test group) and without (control group) the ZCF nanoparticles. This was followed by composite resin build-up and µTBS testing, MMP activity assays, and evaluation of the antibacterial effects. The results showed no significant differences in the µTBS between the ZCF and the control groups. However, the ZCF exhibited a significant inhibitory effect against MMP-2, MMP-8, and MMP-9, in addition to an antibacterial effect on Streptococcus mutans. Therefore, the present study demonstrated that the addition of ZCF nanoparticles to adhesive systems can result in MMP inhibition and antibacterial action while maintaining the mechanical properties of the bonding restorations.

Several desensitizers routinely used clinically for dentin hypersensitivity are expected to inhibit demineralization. This study aimed to evaluate the effectiveness of sealing materials in inhibiting demineralization and increasing fluorine (F) uptake by acid-treated root surfaces. Five noncarious extracted human teeth were used to produce specimens. Three different fluoride-containing materials, namely “MS Coat F” (MS), “MS Coat Hys Block Gel” (HS), and CTX2 Varnish (FV), were used herein. Each material was applied to the demineralized root surface. Single sections were obtained from each specimen. All surfaces of each specimen, except the polished surface, were covered with wax and immersed in an automatic pH cycling system for 2 weeks. Fluorine and calcium distributions in the carious lesions of each specimen were evaluated using proton-induced gamma emission (PIGE) and X-ray (PIXE) techniques, respectively. Dentin demineralization was analyzed using transverse microradiography (TMR) before and after pH cycling. µPIXE/PIGE analysis demonstrated that all sample groups showed increased fluoride uptake on the root surface. TMR analysis revealed that both HS and FV showed significantly lower integrated mineral loss values than the control group. All three samples demonstrated a tendency towards increased fluoride uptake from fluoride-containing hypersensitivity desensitizers and a demineralization inhibition effect on root dentin.

This study aimed to use an in-air micro-particle-induced X-ray/gamma emission (in-air µPIXE/PIGE) system to evaluate tooth-bound fluoride (T-F) in dentin following the application of fluoride-containing tooth-coating materials. Three fluoride-containing coating materials (PRG Barrier Coat, Clinpro XT varnish, and Fuji IX EXTRA) and a control were applied to the root dentin surface of human molars (n = 6, total 48 samples). Samples were stored in a remineralizing solution (pH 7.0) for 7 or 28 days and then sectioned into two adjacent slices. One slice of each sample was immersed in 1M potassium hydroxide (KOH) solution for 24 h and rinsed with water for 5 min for the T-F analysis. The other slice did not undergo KOH treatment and was used to analyze the total fluoride content (W-F). The fluoride and calcium distributions were measured in all the slices using an in-air µPIXE/PIGE. Additionally, the amount of fluoride released from each material was measured. Clinpro XT varnish demonstrated the highest fluoride release among all the materials and tended to show high W-F and T-F and lower T-F/W-F ratios. Our study demonstrates that a high fluoride-releasing material shows high fluoride distribution into the tooth structure and low conversion from fluoride uptake by tooth-bound fluoride.

Certain dentin hypersensitivity treatment materials include oxalic acid to coat dentin surfaces with minerals, while certain organic acids possess a remineralization effect. Herein, an organic acid that inhibits the demineralization and coating of root surfaces was evaluated. Specimens were produced using five non-carious extracted bovines. Four different acids were used: oxalic acid (OA), malonic acid (MA), polyacrylic acid (PA), and succinic acid (SA). Each acid was applied to the root surface and washed using distilled water or a remineralization solution, and the surface was observed using scanning electron microscopy (SEM). All the surfaces of each specimen, barring the polished surface, were covered with wax and immersed in an automatic pH cycling system for two weeks. Dentin demineralization was analyzed using transverse microradiography (TMR) before and after pH cycling. SEM analysis demonstrated that the three acid groups demineralized the dentin surface, whereas the OA group generated crystals covering the dentin surface, even in a distilled water environment. TMR analysis revealed that the OA groups showed significantly lower integrated mineral loss compared with the other groups, even in the distilled water environment. The results suggest that OA generates insoluble calcium oxalate crystals on the dentin and suppresses demineralization even under low saliva conditions.

The development of multifunctional materials has been expected in dentistry. This study investigated the effects of a novel universal bond containing a bioactive monomer, calcium 4-methacryloxyethyl trimellitic acid (CMET), on odontoblast differentiation in vitro. Eluates from bioactive universal bond with CMET (BA (+), BA bond), bioactive universal bond without CMET (BA (−)), and Scotchbond Universal Plus adhesive (SC, 3M ESPE, USA) were added to the culture medium of the rat odontoblast-like cell line MDPC-23. Then, cell proliferation, differentiation, and mineralization were examined. Statistical analyses were performed using a one-way ANOVA and Tukey’s HSDtest. The cell counting kit-8 assay and alkaline phosphatase (ALP) assay showed that cell proliferation and ALP were significantly higher in the 0.5% BA (+) group than in the other groups. In a real-time reverse-transcription polymerase chain reaction, mRNA expression of the odontogenic markers, dentin sialophosphoprotein (DSPP) and dentin matrix protein-1 (DMP-1), was significantly higher in the 0.5% BA (+) group than in the BA (−) and SC groups. Calcific nodule formation in MDPC-23 cells was accelerated in the BA (+) group in a dose-dependent manner (p < 0.01); however, no such effect was observed in the BA (−) and SC groups. Thus, the BA bond shows excellent potential for dentin regeneration.