This study was aimed at investigating the protective effects of glass ionomer cement (GIC) and surface pre-reacted glass ionomer (S-PRG) fillers used as dental restorative materials on demineralization of bovine enamel. GlasIonomer FX ULTRA (FXU), Fuji IX GP Extra (FIXE), CAREDYNE RESTORE (CDR) were used as GICs. PRG Barrier Coat (BC) was used as the S-PRG filler. They were incubated in a lactic acid solution (pH = 4.0) for six days at a temperature of 37 °C. The mineral was etched from the enamel surface, and a large number of Ca and P ions were detected in solution. The Al, F, Na, Sr, and Sr ions were released in GICs and S-RPG fillers. The Zn ion was released only in CDR and the B ion was released only in BC. The presence of apparent enamel prism peripheries was observed after six days of treatment for the group containing only enamel blocks. pH values for the FXU, FIXE, CDR, BC, and enamel block groups after six days were 6.5, 6.6, 6.7, 5.9, and 5.1, respectively. Therefore, the observed pH neutralization effect suppressed progression of caries due to the release of several ions from the restoratives.

Despite recent advances in bonding restorations, which are the basis of restorative dentistry, secondary caries are still able to form. Previously, a novel fluoride-containing zinc and copper (ZCF) nanocomposite was introduced to prevent the formation of caries due to its antibacterial activity. In this study, we studied the impact of ZCF nanoparticles on the adhesive strength of bonding restorations through micro-tensile bond strength (µTBS) testing. The impact of antibacterial and matrix metalloproteinase (MMP) inhibitors on the nanoparticles was also examined. The nanocomposites were prepared using a simple one-step homogeneous co-precipitation method at a low temperature. A self-etch adhesive was applied to 10 extracted caries-free human molars with (test group) and without (control group) the ZCF nanoparticles. This was followed by composite resin build-up and µTBS testing, MMP activity assays, and evaluation of the antibacterial effects. The results showed no significant differences in the µTBS between the ZCF and the control groups. However, the ZCF exhibited a significant inhibitory effect against MMP-2, MMP-8, and MMP-9, in addition to an antibacterial effect on Streptococcus mutans. Therefore, the present study demonstrated that the addition of ZCF nanoparticles to adhesive systems can result in MMP inhibition and antibacterial action while maintaining the mechanical properties of the bonding restorations.

We investigated the protective effects of glass ionomer cement (GIC) and surface pre-reacted glass ionomer (S-PRG) fillers used as dental restorative materials on the demineralization of bovine enamel during the incubation in a lactic acid solution with pH = 4.0 conducted for 6 d at a temperature of 37 °C. Scanning electron microscopy images of the specimen surfaces from the group containing only enamel blocks revealed the presence of apparent enamel prism peripheries after 6 d of treatment. The mineral was etched from the enamel surface, and a large number of Ca ions were detected in solution. In contrast, the enamel blocks incubated together with discs of GIC or S-PRG fillers did not exhibit demineralized surfaces, owing to the neutralization of the acid solution by the fillers within the first 3 h of the incubation process. The observed pH neutralization effect was attributed to the release of different ions from the fillers and could be utilized for suppressing the progression of caries.

The treatment of damaged enamel surfaces involves modification of the enamel surface with artificial materials or the development of a pseudo-enamel, with research focusing on bioactive and biomimetic materials. In this study, a bioactive auto-polymerizing resin (APR) was developed by adding surface-pre-reacted glass ionomer (S-PRG) fillers of different quantities to APR. Its bioactive effects were evaluated via pH neutralization, ion release, and inhibition of enamel demineralization studies. The pH and fluoride ion release were measured using ion-specific electrodes, revealing that the APR disk with the S-PRG filler immediately neutralized the lactic acid solution (pH 4.0) through ion release. Inductively coupled plasma atomic emission spectrometry revealed that the Sr ion release peaked on the first day, with the other ions following the order F > B > Si > Al > Na, exhibiting a weekly decrease in the same order. Scanning electron microscopy was used to examine the enamel block morphology of the disks after 7 d of incubation, revealing enamel demineralization in disks without the S-PRG filler, whereas no demineralization occurred in disks with the S-PRG filler. APR containing the S-PRG filler demonstrated acid buffering suppressed enamel demineralization and bioactive properties.

Hydroxyapatite (HA) coatings on titanium implants enhance rapid bone formation around the implant due to their osteoconductive property. The present study aimed to achieve a thin and uniform HA film coating on titanium implants by solution plasma treatment (SPT). Commercially pure titanium and porous titanium disks were employed. A pulse plasma generator was used on the disks for 30 min. Morphologic and crystallographic features of the deposited films were examined by scanning electron microscopy (SEM) and X-ray diffractometry (XRD). To evaluate the wettability of the disks, water droplet (20 µL) surfaces were measured using a contact angle analyzer. The initial attachment of osteoblast-like cells (MC3T3E1) on the titanium substrates before and after solution plasma treatment was evaluated by counting the number of attached cells after incubation for 4 h. After immersion in the mineralizing solution for up to seven days, no crystals were observed on the polished-Ti surface. A more uniform and dense precipitation of round and grown crystals with diameters of approximately 1–5 µm was observed on Ti-SPT. XRD clearly showed that the precipitated crystals on titanium disks were HA. The contact angle of the polished-Ti increased with time (θ = 37°–51°). The surface of the Ti-SPT remained hydrophilic (θ ˂ 5°) after up to 30 days of aging. The number of attached cells on the Ti-SPT after aging for 30 days remained above 85% of that on the Ti-SPT without aging. SPT in a mineralizing solution can be used to acquire a homogenous precipitation of HA on porous-surfaced titanium implants.

This study aimed to use intact mineral trioxide aggregate (MTA) as a root canal sealer by hydrophilizing the gutta-percha (GP) surface. The GP specimens were treated with atmospheric air plasma, cetylpyridinium chloride (CPC), or a combination of both. The wettability and surface chemical properties were evaluated using contact angle measurements and X-ray photoelectron spectroscopy (XPS). The physicochemical properties of MTA mixed with water or 100 mM of CPC solution were evaluated using setting time, flowability, compressive strength, and X-ray diffraction (XRD) analyses. Sealing ability was assessed by evaluating the dye penetration in obturated single-rooted teeth. Combined plasma and CPC treatment significantly decreased the contact angle of GP compared to that of the untreated group (p < 0.05) and showed the least hydrophobic recovery after 8 weeks. The XPS analysis confirmed the adsorption of CPC onto the GP surface. The XRD and compressive strength results indicated that the CPC did not interfere with the setting reaction of intact MTA, although the setting time was prolonged (p < 0.05). Dye penetration was significantly reduced in the plasma- and CPC-treated GP groups compared to the untreated GP group (p < 0.05), with a sealing ability comparable to that of the zinc oxide-based sealer.