Photodetectors for the ultraviolet (UV) range of the electromagnetic spectrum are in great demand for several technologies, but require the development of novel device structures and materials. Here we report on the high detectivity of UV photodetectors based on well-ordered laterally mesoporous GaN. The specific detectivity of our devices under UV-illumination reaches values of up to 5.3 × 10¹⁴ Jones. We attribute this high specific detectivity to the properties of the mesoporous GaN/metal contact interface: the trapping of photo-generated holes at the interface lowers the Schottky barrier height thus causing a large internal gain. High detectivity along with a simple fabrication process endows these laterally mesoporous GaN photodetectors with great potential for applications that require selective detection of weak optical signals in the UV range.

Magnetic tunnel junctions (MTJs) with conventional bulk ferromagnets separated by a nonmagnetic insulating layer are key building blocks in spintronics for magnetic sensors and memory. A radically different approach of using atomically-thin van der Waals (vdW) materials in MTJs is expected to boost their figure of merit, the tunneling magnetoresistance (TMR), while relaxing the lattice-matching requirements from the epitaxial growth and supporting high-quality integration of dissimilar materials with atomically-sharp interfaces. We report TMR up to 192% at 10 K in all-vdW Fe₃GeTe₂/GaSe/Fe₃GeTe₂ MTJs. Remarkably, instead of the usual insulating spacer, this large TMR is realized with a vdW semiconductor GaSe. Integration of semiconductors into the MTJs offers energy-band-tunability, bias dependence, magnetic proximity effects, and spin-dependent optical-selection rules. We demonstrate that not only the magnitude of the TMR is tuned by the semiconductor thickness but also the TMR sign can be reversed by varying the bias voltages, enabling modulation of highly spin-polarized carriers in vdW semiconductors.

We have fabricated GaN-based light-emitting diodes (LEDs) with different quantum well (QW) thicknesses to investigate the influence of the quantum confined Stark effect (QCSE) and carrier localization effect on the carrier recombination processes under both direct current (DC) and alternating current (AC) biases. At low current density, QCSE dominates the carrier recombination and decreases the radiative recombination rate. With increasing the current density, QCSE will be screened by injected carriers, and both optical power and modulation bandwidth can be increased. When the polarization field is completely compensated, the carrier localization effect starts to dominate. By reducing the influence of the QCSE and carrier localization effect, a high modulation bandwidth of ∼700 MHz was achieved at a low current density of 425 A/cm² for the LED with 5 nm QW. Our findings will pave an alternative solution for co-optimization of the modulation bandwidth and efficiency for LEDs at a relatively low current density for visible light communications.