Nanoparticles of manganese perovskite of the composition La(0.75)Sr(0.25)MnO(3) uniformly coated with silica were prepared by encapsulation of the magnetic cores (mean crystallite size 24 nm) using tetraethoxysilane followed by fractionation. The resulting hybrid particles form a stable suspension in an aqueous environment at physiological pH and possess a narrow hydrodynamic size distribution. Both calorimetric heating experiments and direct measurements of hysteresis loops in the alternating field revealed high specific power losses, further enhanced by the encapsulation procedure in the case of the coated particles. The corresponding results are discussed on the basis of complex characterization of the particles and especially detailed magnetic measurements. Moreover, the Curie temperature (335 K) of the selected magnetic cores resolves the risk of local overheating during hyperthermia treatment.

The present study reveals the potential of magnetic nanoparticles based on the La_0.75Sr_0.25MnO₃ perovskite manganite for magnetic resonance imaging (MRI). Moreover, it describes the development of the dual imaging probe where the magnetic cores are combined with a fluorescent moiety while the improved colloidal stability is achieved by a two-ply silica shell. At first, the magnetic cores of La_0.75Sr_0.25MnO₃ are coated with a hybrid silica layer, comprising a covalently attached fluorescein moiety that is subsequently covered by a pure silica layer providing the enhanced stability. The detailed characterization of the intermediate and the final product reveals the importance of the complex two-ply shell. Viability tests show that the complete particles are suitable for biological studies. Internalization of the particles and their presence in intracellular vesicles are observed by fluorescence microscopy in different cell types. Further experiments prove no fatal interference with the vitality and insulin releasing ability of labeled pancreatic islets. Relaxometric measurements confirm high spin–spin relaxivities at magnetic fields of B₀ = 0.5–3 T, while visualisation of in vitro labeled pancreatic islets by MRI is successfully tested.