Spruce (Piceaabies) wood hemicelluloses have been obtained by the noncatalytic and catalytic oxidative delignification in the acetic acid-water-hydrogen peroxide medium in a processing time of 3–4 h and temperatures of 90–100 °C. In the catalytic process, the H₂SO₄, MnSO₄, TiO₂, and (NH₄)₆Mo₇O₂₄ catalysts have been used. A polysaccharide yield of up to 11.7 wt% has been found. The hemicellulose composition and structure have been studied by a complex of physicochemical methods, including gas and gel permeation chromatography, Fourier-transform infrared spectroscopy, and thermogravimetric analysis. The galactose:mannose:glucose:arabinose:xylose monomeric units in a ratio of 5:3:2:1:1 have been identified in the hemicelluloses by gas chromatography. Using gel permeation chromatography, the weight average molar mass M_w of hemicelluloses has been found to attain 47,654 g/mol in noncatalytic delignification and up to 42,793 g/mol in catalytic delignification. Based on the same technique, a method for determining the α and k parameters of the Mark–Kuhn–Houwink equation for hemicelluloses has been developed; it has been established that these parameters change between 0.33–1.01 and 1.57–472.17, respectively, depending on the catalyst concentration and process temperature and time. Moreover, the FTIR spectra of the hemicellulose samples contain all the bands characteristic of heteropolysaccharides, specifically, 1069 cm⁻¹ (C–O–C and C–O–H), 1738 cm⁻¹ (ester C=O), 1375 cm⁻¹ (–C–CH₃), 1243 cm⁻¹ (–C–O–), etc. It has been determined by the thermogravimetric analysis that the hemicelluloses isolated from spruce wood are resistant to heating to temperatures of up to ~100 °C and, upon further heating, start destructing at an increasing rate. The antioxidant activity of the hemicelluloses has been examined using the compounds simulating the 2,2-diphenyl-2-picrylhydrazyl free radicals.

In this study, hemicelluloses of aspen wood (Pópulus trémula) were obtained by oxidative delignification in an acetic acid‒water‒hydrogen peroxide medium at temperatures of 70‒100 °C and a process time of 1‒4 h. The maximum polysaccharide yield of up to 9.68 wt% was reported. The composition and structure of the hemicelluloses were studied using a complex of physicochemical methods: gas and gel permeation chromatography, Fourier-transform infrared spectroscopy, 2D nuclear magnetic resonance spectroscopy, and thermogravimetric analysis. The xylose, mannose, galactose, and glucose monomer units were identified in the hemicelluloses by gas chromatography. The weight average molecular weight M_w of the products determined by gel permeation chromatography was found to range within 8932‒33,142 g/mol. The reported Fourier-transform spectra of the hemicelluloses contain all the bands characteristic of heteropolysaccharides; a weak lignin absorption signal in the spectra at 1500‒1510 cm⁻¹ is attributed to a minor content of phenolic fragments in the structure of the obtained hemicelluloses. The use of thermogravimetric analysis established that the hemicelluloses isolated from aspen wood are resistant against heating to temperatures of up to 90–100 °C and, upon further heating up to 400 °C, start destructing at an increasing rate. The antioxidant activity of the hemicelluloses was examined using the compounds that mimic free radicals (1,1-diphenyl-2-picrylhydrazyl) and hydroxyl radicals (salicylic acid). It was found that the activity of all polysaccharides in neutralizing DPPH and hydroxyl radicals is lower than the absorption capacity of vitamin C at all the tested concentrations (0.5, 2, and 5 mg/mL) and attains 81.7 and 82.9%, respectively.

The conventional way of producing microcrystalline cellulose (MCC) from wood raw materials is multistage; it is based on integrating the environmentally hazardous processes of pulping and...

Cellulose sulfates are important biologically active substances with a wide range of useful properties. The development of new methods for the production of cellulose sulfates is an urgent task. In this work, we investigated ion-exchange resins as catalysts for the sulfation of cellulose with sulfamic acid. It has been shown that water-insoluble sulfated reaction products are formed in high yield in the presence of anion exchangers, while water-soluble products are formed in the presence of cation exchangers. The most effective catalyst is Amberlite IR 120. According to gel permeation chromatography, it was shown that the samples sulfated in the presence of the catalysts KU-2-8, Purolit s390 plus, and AN-31 SO₄²⁻ underwent the greatest degradation. The molecular weight destribution profiles of these samples are noticeably shifted to the left towards low-molecular-weight compounds with an increase in fractions in the regions Mw ~2.100 g/mol and ~3.500 g/mol, indicating the growth of microcrystalline cellulose depolymerization products. The introduction of a sulfate group into the cellulose molecule is confirmed using FTIR spectroscopy by the appearance of absorption bands at 1245–1252 cm⁻¹ and 800–809 cm⁻¹, which correspond to the vibrations of the sulfate group. According to X-ray diffraction data, amorphization of the crystalline structure of cellulose is observed during sulfation. Thermal analysis has shown that with an increase in the content of sulfate groups in cellulose derivatives, thermal stability decreases.