In this work, a polyaniline/lead sulfide (PANI/PbS) nanocomposite was prepared by combining the in situ oxidation polymerization method and the surface adsorption process. This nanocomposite was applied as a supercapacitor electrode. The crystal structure, nanomorphology, and optical analysis of PANI and PANI/PbS were investigated. The electrochemical performance of the designed PANI/PbS electrode-based supercapacitor was tested by using cyclic voltammetry (CV), chronopotentiometry (CP), and AC impedance techniques in HCl and Na₂SO₄ electrolytes. The average crystallite size of the PANI/PbS nanocomposite is about 43 nm. PANI/PbS possesses an agglomerated network related to PANI with additional spherical shapes from PbS nanoparticles. After the PANI/PbS nanocomposite formation, there are enhancements in their absorption intensities. At a current density of 0.4 A g⁻¹, the specific capacitance of PANI/PbS in Na₂SO₄ and HCl was found to be 303 and 625 F g⁻¹, respectively. In HCl (625 F g⁻¹ and 1500 mF cm⁻²), the gravimetric and areal capacitances of the PANI/PbS electrode are nearly double those of the Na₂SO₄ electrolyte. Also, the average specific energy and specific power density values for the PANI/PbS electrode in HCl are 4.168 Wh kg⁻¹ and 196.03 W kg⁻¹, respectively. After 5000 cycles, the capacitance loses only 4.5% of its initial value. The results refer to the high stability and good performance of the designed PANI/PbS as a supercapacitor electrode.

Thin films of ZnO and ZnO/carbon nanotubes (CNTs) are prepared and used as CO₂ gas sensors. The spray pyrolysis method was used to prepare both ZnO and ZnO/CNTs films, with CNTs first prepared using the chemical vapor deposition method (CVD). The chemical structure and optical analyses for all the prepared nanomaterials were performed using X-ray diffraction (XRD), Fourier transformer infrared spectroscopy (FTIR), and UV/Vis spectrophotometer devices, respectively. According to the XRD analysis, the crystal sizes of ZnO and ZnO/CNTs were approximately 50.4 and 65.2 nm, respectively. CNTs have average inner and outer diameters of about 3 and 13 nm respectively, according to the transmitted electron microscope (TEM), and a wall thickness of about 5 nm. The detection of CO₂ is accomplished by passing varying rates of the gas from 30 to 150 sccm over the prepared thin-film electrodes. At 150 sccm, the sensitivities of ZnO and ZnO/CNTs sensors are 6.8% and 22.4%, respectively. The ZnO/CNTs sensor has a very stable sensitivity to CO₂ gas for 21 days. Moreover, this sensor has a high selectivity to CO₂ in comparison with other gases, in which the ZnO/CNTs sensor has a higher sensitivity to CO₂ compared to H₂ and C₂H₂.

TiO₂ is one of the most investigated materials due to its abundance, lack of toxicity, high faradaic capacitance, and high chemical and physical stability; however, its potential use in energy storage devices is constrained by its high internal resistance and weak van der Waals interaction between the particles. Carbon nanotubes are especially well suited for solving these issues due to their strong mechanical strength, superior electrical conductivity, high electron mobilities, excellent chemical and thermal stability, and enormous specific nanoporous surface. The hydrothermal approach was followed by chemical vapor deposition to produce a network composite of titanium dioxide nanoribbons (TNRs) and multi-walled carbon nanotubes (MWCNTs). The nanocomposite was characterized using a variety of methods. One phase of TiO₂-B nanoribbons has porous pits on its surface, and MWCNTs are grown in these pits to produce a network-like structure in the nanocomposite. With a two-electrode supercapacitor configuration, the TNR/CNT gave a gravimetric capacitance of 33.33 F g⁻¹, which was enhanced to 68.18 F g⁻¹ in a redox-active electrolyte containing hydroquinone (HQ). Additionally, the areal capacitance per footprint was increased from 80 mF cm⁻² in H₂SO₄ to 163.63 mF cm⁻² in H₂SO₄/HQ. The TNR/CNT supercapacitor has superior cyclic stability than the previously reported TiO₂-based electrodes, with 97.5% capacitance retention after 5000 cycles. Based on these results, it looks like the TNR/CNT supercapacitor could provide portable electronic power supplies with new ways to work in the future.

In this work, three nanoparticle samples, Ni₄Co₂Pt/CNFs, Ni₅CoPt/CNFs and Ni₆Pt/CNFs, were designed according to the molar ratio during loading on carbon nanofibers (CNFs) using electrospinning and carbonization at 900 °C for 7 h in an argon atmosphere. The metal loading and carbon ratio were fixed at 20 and 80 wt%, respectively. Various analysis tools were used to investigate the chemical composition, structural, morphological, and electrochemical (EC) properties. For samples with varying Co%, the carbonization process reduces the fiber diameter of the obtained electrospun nanofibers from 200–580 nm to 150–200 nm. The EDX mapping revealed that nickel, platinum, and cobalt were evenly and uniformly incorporated into the carbonized PVANFs. The prepared Ni-Co-Pt/CNFs have a face-centered cubic (FCC) structure with slightly increased crystallite size as the Co% decreased. The electrocatalytic properties of the samples were investigated for ethanol, methanol and urea electrooxidation. Using cyclic voltammetry (CV), chronoamperometry, and electrochemical impedance measurements, the catalytic performance and electrode stability were investigated as a function of electrolyte concentration, scan rate, and reaction time. When Co is added to Ni, the activation energy required for the electrooxidation reaction decreases and the electrode stability increases. In 1.5 M methanol, the Ni₅CoPt/CNFs electrode showed the lowest onset potential and the highest current density (30.6 A/g). This current density is reduced to 28.2 and 21.2 A/g for 1.5 M ethanol and 0.33 M urea, respectively. The electrooxidation of ethanol, methanol, and urea using our electrocatalysts is a combination of kinetic/diffusion control limiting reactions. This research provided a unique approach to developing an efficient Ni-Co-Pt-based electrooxidation catalyst for ethanol, methanol and urea.