The main challenge associated with the application of selective laser melting (SLM) to Ni based superalloys is the performance of process optimisation to maximise the mechanical properties. The energy density parameter has typically been used as a semiquantitative approach to identify the energy threshold beyond which the material achieves virtually full consolidation. Nonetheless, some Ni superalloys are susceptible to crack formation during SLM, which cannot be avoided via process optimisation. In the present report, a comparative study is presented showing the utility of the energy density parameter in process optimisation for γ′ and γ′/γ″ strengthened Ni based superalloys. For both classes, it was found that the build density increases [i.e. void area () decreases] with the increase in the energy density. Nonetheless, no direct correlation can be found between the energy density parameter and the cracking density.

One of the main challenges in additive manufacturing (AM) of medical implants for the treatment of bone tissue defects is to optimise the mechanical and biological performance. The use of post-processing can be a necessity to improve the physical properties of customised AM processed implants. In this study, Ti-6Al-4V coupons were manufactured using selective laser melting (SLM) in two build orientations (vertical and horizontal) and subsequently post-processed using combinations of hot isostatic pressing (HIP), sandblasting (SB), polishing (PL) and chemical etching (CE). The effect of the different post-manufacturing strategies on the tensile and fatigue performance of the SLMed parts was investigated and rationalised by observing the surface topography. Vertically built samples showed higher yield strength (YS) and ultimate tensile strength (UTS) than the horizontal samples, increasing from 760.9 ± 22.3 MPa and 961.3 ± 50.2 MPa in the horizontal condition to 820.09 ± 16.5 MPa and 1006.7 ± 6.3 MPa in the vertical condition, respectively. After the HIP treatment, the ductility was substantially improved in both orientations; by 2.1 and 2.9 folds in the vertical and horizontal orientations, respectively. The vertically built samples demonstrated a superior ductility of 22% following HIP and polishing. Furthermore, chemical etching was found to be the most effective surface post-processing treatment to improve the fatigue performance after HIP, achieving the highest run-out strength of 450 MPa. Most importantly, chemical etching after HIP enhanced the cellular affinity of the surface, in addition to its good fatigue performance, making it a promising post-processing approach for bone implants where tissue integration is needed.

The rise of antibiotic resistant bacterial species is driving the requirement for medical devices that minimise infection risks. Antimicrobial functionality may be achieved by modifying the implant design to incorporate a reservoir that locally releases a therapeutic. For this approach to be successful it is critical that mechanical functionality of the implant is maintained. This study explores the opportunity to exploit the design flexibilities possible using additive manufacturing to develop porous lattices that maximise the volume available for drug loading while maintaining load-bearing capacity of a hip implant. Eight unit cell types were initially investigated and a volume fraction of 30% was identified as the lowest level at which all lattices met the design criteria in ISO 13314. Finite element analysis (FEA) identified three lattice types that exhibited significantly lower displacement (10-fold) compared with other designs; Schwartz primitive, Schwartz primitive pinched and cylinder grid. These lattices were additively manufactured in Ti-6Al-4V using selective laser melting. Each design exceeded the minimum strength requirements for orthopaedic hip implants according to ISO 7206-4. The Schwartz primitive (Pinched) lattice geometry, with 10% volume fill and a cubic unit cell period of 10, allowed the greatest void volume of all lattice designs whilst meeting the fatigue requirements for use in an orthopaedic implant (ISO 7206-4). This paper demonstrates an example of how additive manufacture may be exploited to add additional functionality to medical implants.