The aim of this paper was to investigate the compression properties of several trabecular structures produced by additive laser manufacturing of a Ti6Al4V, having different densities and unit cells. Filling space structures were investigated, with different unit cells characterized by both bending-dominated and stretching-dominated behaviour. The stiffness and yield strength were correlated to relative density according to the Gibson and Ashby model. For a constant porosity, the stiffness and the yield strength varied between two extremes represented by the cubic structure (stretching-dominated deformation) and the cross structure (bending-dominated deformation). The properties of the deformed structures did not differ substantially from those of the regular structures. Only in the cubic structure did distortion enhance the contribution of bending to deformation and both stiffness and strength decreased. Cross structures displayed the highest strength at constant stiffness than the others, since they are characterized by the most favourable orientation of the struts.

In this chapter, a three-dimensional finite element model is developed to simulate the thermal behavior of the molten pool in selective laser melting (SLM) process. Laser-based additive manufacturing (AM) is a near net shape manufacturing process able to produce 3D objects. They are layer-wise built through selective melting of a metal powder bed. The necessary energy is provided by a laser source. The interaction between laser and material occurs within a few microseconds, hence the transient thermal behavior must be taken into account. A calibration procedure is carried out to fit the numerical solution with the experimental data. Once the calibration has corrected the thermal parameters, a dynamic mesh refinement is applied to reduce the computational cost. The scanning strategy adopted by the laser is simulated by a path simulator built using MatLab®, while numerical analysis is carried out using ANSYS®, a commercial finite element software. To improve the performance of the simulation, the two codes interact each other to solve the analysis. Temperature distribution and geometrical feature of the molten pool under different process conditions are investigated. Results from the FE analysis provide guidance for setting up the optimization of process parameters and develop a base for further residual stress analysis.

The influence of the main process parameters, laser power, point distance and time exposure, on the surface microgeometry of Ti6Al4V specimens produced by a pulsed powder bed fusion process was investigated. A 3D characterization was carried out and collected data were elaborated to reconstruct the surface and to determine both the 3D and the 2D material ratio curves along different directions. The 3D material ratio curve gives a slightly lower material ratio of peak zone Mr1 and higher material ratio of valley zone Mr2, reduced peak height Rpk and reduced valley height Rvk than the 2D curves. Roughness is greater in the 3D analysis than in the 2D one, skewness is the same and kurtosis increases from 3 in 3D. Roughness and skewness increase on increasing point distance and decreasing time exposure and laser power. Within the investigated ranges (27.3–71.2 J/mm³), an increase in energy density reduces the surface roughness while skewness and kurtosis are not significantly affected. The results indicate that a 3D approach allows better characterization of the surface microgeometry than a 2D one.