Composite materials with carbon and glass fibers in an epoxy matrix are widely used systems due to their excellent mechanical parameters, and machining is a standard finishing operation in their manufacture. Previous studies focused exclusively on the characteristics of the fibers released into the air. This work aimed to analyze the nature of the material waste that remains on the work surface after machining. The dust on the work surface is made up of fibers and a polymer matrix, and due to its dimensions and chemical stability, it is a potentially dangerous inhalable material currently treated as regular waste. The smallest sizes of destroyed carbon fibers were generated during drilling and grinding (0.1 μm), and the smallest glass fiber particles were generated during milling (0.05 μm). Due to their nature, carbon fibers break by a tough fracture, and glass fibers by a brittle fracture. In both cases, the rupture of the fibers was perpendicular to or at an angle to the longitudinal axis of the fibers. The average lengths of destroyed carbon fibers from the tested processes ranged from 15 to 20 µm and 30 to 60 µm for glass fibers.

Glass fibers are often used as reinforcing fibers in reinforced polymers. Composites reinforced with glass fibers (GFRP) stand out with excellent mechanical and physical properties applicable to industrial practice. Machining these composites requires the correct choice of tools and cutting conditions so that the machined surface shows good properties, there is no fiber delamination, thermal stress on the workpiece and the tool, or excessive tool wear. The study was devoted to circumferential milling of fabric-bonded GFRP plates, in which attention was paid to the influence of the abrasive effect of glass fibers on wear and tool life. Attention was also paid to surface roughness after machining, material delamination, and forces during machining were measured. Three end mills of the same diameter with different coatings, number of teeth, and geometry were selected for the study. This choice of tools was intended to achieve various accompanying and subsequent phenomena that were investigated. Milling was performed on a CNC milling center under preselected cutting conditions. The paper summarizes information on fiber delamination and machined laminate damage after milling, tool wear, and surface roughness parameters as a function of tool wear. This paper provides an opportunity for researchers to increase their knowledge of specific aspects of milling GFRP composites, whether with a tool specifically designed for this or not.

This study aimed to investigate the effect of the clearance angle of the milling tool on wear, cutting forces, machined edge roughness, and delamination during non-contiguous milling of carbon-fiber-reinforced plastic (CFRP) composite panels with a twill weave and 90° fiber orientation. To achieve the objective of the study, it was first necessary to design suitable tools (6 mm diameter sintered carbide shank milling cutters) with a variety of clearance angles (8.4°, 12.4°, and 16.4°) and all the machinery and measuring equipment for the research to be carried out. Furthermore, measurement and evaluation methods for cutting tool wear, cutting forces, machined edge roughness, and delamination were developed. Last but not least, the results obtained during the research were summarized and evaluated. From the experiments conducted in this study, it was found that the tool clearance angle has a significant effect on tool wear, roughness of the machined surface, and delamination of the carbon fiber composite board. The tool with a clearance angle of 8.4° wore faster than the tool with a clearance angle of 16.4°. The same trend was observed for cutting force, machined surface roughness, and delamination. In this context, it was also shown that the cutting force increased as the tool wear increased, which in turn increased surface roughness and delamination. These results are of practical significance, not only in terms of the quality of the machined surface but also in terms of time, cost, and energy savings when machining CFRP composite materials.

Conventional dry machining (without process media) of carbon fibre composite materials (CFRP) produces tiny chips/dust particles that float in the air and cause health hazards to the machining operator. The present study investigates the effect of cutting conditions (cutting speed, feed per tooth and depth of cut) during CFRP milling on the size, shape and amount of harmful dust particles. For the present study, one type of cutting tool (CVD diamond-coated carbide) was used directly for machining CFRP. The analysis of harmful dust particles was carried out on a Tescan Mira 3 (Tescan, Brno, Czech Republic) scanning electron microscope and a Keyence VK-X 1000 (Keyence, Itasca, IL, USA) confocal microscope. The results show that with the combination of higher feed per tooth (mm) and lower cutting speed, for specific CFRP materials, the size and shape of harmful dust particles is reduced. Particles ranging in size from 2.2 to 99 μm were deposited on the filters. Smaller particles were retained on the tool body (1.7 to 40 μm). Similar particle sizes were deposited on the machine and in the work area.

The present study focuses on the elimination of delamination during the drilling of a linen-based biocomposite material in epoxy resin used for the manufacture of sports kayaks, depending on the tool material, cutting conditions, and the use of additional wooden support plates. In the present study, HSS (high-speed steel) and Carbide cutting tools without coatings, with the same geometry and two types of cutting conditions (n = 1500 rpm, f_n = 0.05 and 0.1 mm/rev) were used. A Sololite-type wooden backing plate was used to aid in reducing delamination. The results show that the additional support plates significantly reduced delamination by up to 80% both at the material inlet and especially at the drill hole outlet. In this study, the use of a lower feed rate (f_n = 0.05 mm/rev) per tooth was shown to have a significant effect on reducing the delamination of biocomposite materials with flax fibers, which are generally known to be difficult to machine. The Carbide cutting tool shows significantly better results both in terms of its wear and in terms of delamination of the biocomposite material. The highest delamination was obtained without the use of a backing board at the tool exit after 50 drilled holes of 3509 µm. With the use of a backing board, this delamination decreased to 693 µm after 50 drilled holes.

Composite materials made of fiber-reinforced plastic laminates are highly susceptible to surface damage caused by wear during contour milling, especially with inappropriate tool and cutting material properties. Improper choice of tools and cutting conditions lead to delamination between applied layers, thermal damage of materials in the polymer matrix, and reduction of the edge quality of cutting tools. The study was devoted to circumferential milling of twill-bonded CFRP (carbon-fiber-reinforced polymer) sheets with a focus on cutting forces and tool flank face wear, including their effect on the machined surface structure, roughness, and topography of the laminate. The main objective of the study is to investigate the feasibility of applying conventional coated tools, which are not primarily designed for milling CFRP, in comparison to a dedicated DLC (diamond-like carbon) coated tool, due to economic and distribution availability and the possibility of providing suitable cutting conditions during milling. The study provides results confirming the possibility of using conventional tools for machining CFRP and provides relevant experimental results that can be implemented for optimal tool selection, tool life criteria, cutting conditions, and machining strategies including low energy consumption. The best values of the investigated parameters were obtained when using the ECSSF (instrument designation) tool with DLC coating.