The reported study concerns the introduction of renewable raw materials into the formulation of rigid polyurethane foams in the quest for the sustainable development of polymer composites. In this study, rigid polyurethane foam composites were prepared using 75 wt.% of rapeseed oil-based polyol and 15 parts per hundred parts of polyol (php) of natural fillers such as chokeberry pomace, raspberry seeds, as well as hazelnut and walnut shells. The influence of the used raw materials on the foaming process, structure, and properties of foams was investigated using a FOAMAT analyzer and a wide selection of characterization techniques. The introduction of renewable raw materials limited reactivity of the system, which reduced maximum temperature of the foaming process. Moreover, foams prepared using renewable raw materials were characterized by a more regular cell structure, a higher share of closed cells, lower apparent density, lower compressive strength and glass transition temperature, low friability (<2%), low water absorption (<1%), high dimensional stability (<±0.5%) and increased thermal stability. The proper selection and preparation of the renewable raw materials and the rational development of the polyurethane recipe composition allow for the preparation of environmentally-friendly foam products with beneficial application properties considering the demands of the circular economy in the synthesis of rigid foams.

This work presents the cell structure and selected properties of polyurethane (PUR) foams, based on two types of hydroxylated used cooking oil and additionally modified with three different flame retardants. Bio-polyols from municipal waste oil with different chemical structures were obtained by transesterification with triethanolamine (UCO_TEA) and diethylene glycol (UCO_DEG). Next, these bio-polyols were used to prepare open-cell polyurethane foams of very low apparent densities for thermal insulation applications. In order to obtain foams with reduced flammability, the PUR systems were modified with different amounts (10–30 parts per hundred polyol by weight—php) of flame retardants: TCPP (tris(1-chloro-2-propyl)phosphate), TEP (triethyl phosphate), and DMPP (dimethyl propylphosphonate). The flame retardants caused a decrease of the PUR formulations reactivity. The apparent densities of all the foams were comparable in the range 12–15 kg/m³. The lowest coefficients of thermal conductivity were measured for the open-cell PUR foams modified with DMPP. The lowest values of heat release rate were found for the foams based on the UCO_TEA and UCO_DEG bio-polyols that were modified with 30 php of DMPP.

The search for new sources of raw materials that can be used in the synthesis of polyurethanes and other polymer groups is extremely important. Currently, according to the principles of green chemistry and a circular economy, waste materials with a high reuse potential are being sought. This article presents a way of obtaining used-cooking-oil-based compounds capable of participating in the reaction of polyurethane creation. The transesterification reaction can be carried out using a variety of homo- and heterogeneous acid or base catalysts. Here, we looked at the impact of selected catalysts on the course of transesterification reactions, the composition of the post-reaction mixture and the possibility of using the products in polyurethane foam synthesis. The raw materials and the products were analyzed by means of gel permeation chromatography, FTIR spectroscopy and ¹H NMR. The polyurethane foam formation process was analyzed using a FOAMAT^® apparatus.

The main strategy of the European Commission in the field of the building industry assumes a reduction of greenhouse gas emissions by up to 20% by 2020 and by up to 80% by 2050. In order to meet these conditions, it is necessary to develop not only efficient thermal insulation materials, but also more environmentally friendly ones. This paper describes an experiment in which two types of bio-polyols were obtained using transesterification of used cooking oil with triethanolamine (UCO_TEA) and diethylene glycol (UCO_DEG). The bio-polyols were next used to prepare low-density rigid polyurethane (PUR) foams. It was found that the bio-polyols increased the reactivity of the PUR systems, regardless of their chemical structures. The reactivity of the system modified with 60% of the diethylene glycol-based bio-polyol was higher than in the case of the reference system. The bio-foams exhibited apparent densities of 41–45 kg/m³, homogeneous cellular structures and advantageous values of the coefficient of thermal conductivity. It was observed that the higher functionality of bio-polyol UCO_TEA compared with UCO_DEG had a beneficial effect on the mechanical and thermal properties of the bio-foams. The most promising results were obtained in the case of the foams modified in 60% with the bio-polyol based on triethanoloamine. In conclusion, this approach, utilizing used cooking oil in the synthesis of high-value thermal insulating materials, provides a sustainable municipal waste recycling solution.

This article presents an ecological approach based on climate neutrality to the synthesis of open-cell polyurethane foams with modified used cooking rapeseed oils. Water was used as a chemical blowing agent in the amount of 20–28 wt.% in relation to the weight of the bio-polyol. The influence of water on the physical and mechanical properties of the synthesized foams was investigated. The resultant porous materials were tested for the content of closed cells, cell structure, apparent density, thermal conductivity, compressive strength, and dimensional stability. It was found that the apparent density decreased in the range of 11–13 kg/m³ when the amount of the foaming agent was increased. In the next step, a foam with a water content of 22% was selected as having the most favorable physico–mechanical properties among all the foams with various water contents. The isocyanate index of the selected foam was then changed from 0.6 to 1.1 and it was observed that the compressive strength increased by an average of 10 kPa. The thermal conductivity coefficients of the final materials with different water contents and isocyanate indices were comparable and in the range of 40–43 mW/m·K.

In order to create greener polyurethane (PUR) foams, modified used cooking oils (UCO) were applied as starting resources for the synthesis of bio-polyols. The bio-polyols were produced using transesterification of UCO with diethylene glycol (UCO_DEG) and triethanolamine (UCO_TEA). Next, open-cell PUR foams were synthesized by replacing 20, 40, 60, 80 and 100% of the petrochemical polyol with the bio-polyol UCO_DEG or UCO_TEA. It was observed that an increasing bio-polyol content (up to 60%) led to an increase of the closed cell content. However, a further increase in the bio-polyol content up to 100% resulted in foam cell opening. The bio-foams obtained in the experiment had an apparent density of 13–18 kg/m³. The coefficient of thermal conductivity was determined at three different average temperatures: 10, 0 and −10 °C. The PUR bio-foams modified with bio-polyol UCO_TEA had lower values of thermal conductivity, regardless of the average temperature (35.99–39.57 mW/m·K) than the foams modified with bio-polyol UCO_DEG (36.95–43.78 mW/m·K). The compressive strength of most of the bio-foams was characterized by a higher value than the compressive strength of the reference material (without bio-polyol). Finally, it was observed that the bio-materials exhibited dimensional stability at 70 °C.