The reported study concerns the introduction of renewable raw materials into the formulation of rigid polyurethane foams in the quest for the sustainable development of polymer composites. In this study, rigid polyurethane foam composites were prepared using 75 wt.% of rapeseed oil-based polyol and 15 parts per hundred parts of polyol (php) of natural fillers such as chokeberry pomace, raspberry seeds, as well as hazelnut and walnut shells. The influence of the used raw materials on the foaming process, structure, and properties of foams was investigated using a FOAMAT analyzer and a wide selection of characterization techniques. The introduction of renewable raw materials limited reactivity of the system, which reduced maximum temperature of the foaming process. Moreover, foams prepared using renewable raw materials were characterized by a more regular cell structure, a higher share of closed cells, lower apparent density, lower compressive strength and glass transition temperature, low friability (<2%), low water absorption (<1%), high dimensional stability (<±0.5%) and increased thermal stability. The proper selection and preparation of the renewable raw materials and the rational development of the polyurethane recipe composition allow for the preparation of environmentally-friendly foam products with beneficial application properties considering the demands of the circular economy in the synthesis of rigid foams.

This paper presents results of research on the preparation of biochar-modified rigid polyurethane foams that could be successfully used as thermal insulation materials. The biochar was introduced into polyurethane systems in an amount of up to 20 wt.%. As a result, foam cells became elongated in the direction of foam growth and their cross-sectional areas decreased. The filler-containing systems exhibited a reduction in their apparent densities of up to 20% compared to the unfilled system while maintaining a thermal conductivity of 25 mW/m·K. Biochar in rigid polyurethane foams improved their dimensional and thermal stability.

This paper presents research into the preparation of rigid polyurethane foams with bio-polyols from rapeseed and tall oil. Rigid polyurethane foams were designed with a cryogenic insulation application for aerospace in mind. The polyurethane systems containing non-renewable diethylene glycol (DEG) were modified by replacing it with rapeseed oil-based low functional polyol (LF), obtained by a two-step reaction of epoxidation and oxirane ring opening with 1-hexanol. It was observed that as the proportion of the LF polyol in the polyurethane system increased, so too did the apparent density of the foam material. An increase in the value of the thermal conductivity coefficient was associated with an increase in the value of apparent density. Mechanical tests showed that the rigid polyurethane foam had higher compressive strength at cryogenic temperatures compared with the values obtained at room temperature. The adhesion test indicated that the foams subjected to cryo-shock obtained similar values of adhesion strength to the materials that were not subjected to this test. The results obtained were higher than 0.1 MPa, which is a favourable value for foam materials in low-temperature applications.

Rigid polyurethane foams (RPURF) containing a bio-polyol from rapeseed oil and different phosphorus-based flame retardants were obtained. Triethyl phosphate (TEP), dimethyl propane phosphonate (DMPP) and cyclic phosphonates Addforce CT 901 (20 parts per hundred polyol by weight) were used in the synthesis of RPURF. The influence of used flame retardants on foaming process, cell structure, and physical–mechanical properties as well as flammability of RPURF were examined. The addition of flame retardants influenced the parameters of the cellular structure and decreased compressive strength. All obtained foam materials had a low thermal conductivity coefficient, which allows them to be used as thermal insulation. The research results of bio-based RPURF were compared with foams obtained without bio-polyol. All modified materials had an oxygen index above 21 vol%; therefore, they can be classified as self-extinguishing materials. The analysis of parameters obtained after the cone calorimeter test showed that the modified RPURF have a lower tendency to fire development compared to the reference foams, which was particularly noticeable for the materials with the addition of DMPP.

The main goal of this work was to evaluate the thermal insulation and sound absorption properties of open-cell rigid polyurethane foams synthesized with different contents of cooking oil-based polyol. The content of the applied bio-polyol as well as flame retardant (triethyl phosphate) in the foam formulation had a significant influence on the cellular structures of the materials. The open-cell polyurethane foams were characterized by apparent densities in the range 16–30 kg/m³. The sound absorption coefficients of the polyurethanes with various contents of bio-polyol were determined using the standing wave method (Kundt’s tube) in the frequency range of 100–6300 Hz. The effect of the content of the bio-polyol and flame retardant on the coefficient of thermal conductivity (at average temperatures of 0, 10 and 20 °C) as well as the compressive strength (at 20 and −10 °C) was analyzed. Different trends were observed in terms of the thermal insulation properties and sound absorption ability of the open-cell polyurethanes due to the addition of bio-polyol. In conclusion, it is necessary to use systems containing both petrochemical and bio-based raw materials.

This work presents the cell structure and selected properties of polyurethane (PUR) foams, based on two types of hydroxylated used cooking oil and additionally modified with three different flame retardants. Bio-polyols from municipal waste oil with different chemical structures were obtained by transesterification with triethanolamine (UCO_TEA) and diethylene glycol (UCO_DEG). Next, these bio-polyols were used to prepare open-cell polyurethane foams of very low apparent densities for thermal insulation applications. In order to obtain foams with reduced flammability, the PUR systems were modified with different amounts (10–30 parts per hundred polyol by weight—php) of flame retardants: TCPP (tris(1-chloro-2-propyl)phosphate), TEP (triethyl phosphate), and DMPP (dimethyl propylphosphonate). The flame retardants caused a decrease of the PUR formulations reactivity. The apparent densities of all the foams were comparable in the range 12–15 kg/m³. The lowest coefficients of thermal conductivity were measured for the open-cell PUR foams modified with DMPP. The lowest values of heat release rate were found for the foams based on the UCO_TEA and UCO_DEG bio-polyols that were modified with 30 php of DMPP.