Yttria-stabilized zirconia (YSZ) is well-known as a material with perfect mechanical, thermal, and electrical properties. It is used for manufacturing various high-temperature components for aerospace and energy generation, as well as wear- and corrosion-resistant devices in medicine. This work investigated the effect of a Y₂O₃ addition to ZrO₂ on the microstructure and mechanical properties of YSZ ceramics produced by one sintering schedule. ZrO₂ ceramics doped with 3, 4, 5, 6, 7, and 8 mol% Y₂O₃ (designated 3YSZ through to 8YSZ) were prepared by using conventional sintering at 1550 °C for 2 h in argon. The effect of yttria content was analyzed with respect to grain size, morphology of the microstructural features, phase composition, parameters of fracture surface, and flexural strength. The 7YSZ ceramics sintered at 1550 °C for 2 h showed the highest level of flexural strength due to the formation of the fine-grained microstructure containing mainly the monoclinic and tetragonal zirconia phases. The fracture micromechanism in the studied YSZ ceramics is discussed.

It is known that the yttria-stabilized zirconia (YSZ) material has superior thermal, mechanical, and electrical properties. This material is used for manufacturing products and components of air heaters, hydrogen reformers, cracking furnaces, fired heaters, etc. This work is aimed at searching for the optimal sintering mode of YSZ ceramics that provides a high crack growth resistance. Beam specimens of ZrO₂ ceramics doped with 6, 7, and 8 mol% Y₂O₃ (hereinafter: 6YSZ, 7YSZ, and 8YSZ) were prepared using a conventional sintering technique. Four sintering temperatures (1450 °C, 1500 °C, 1550 °C, and 1600 °C) were used for the 6YSZ series and two sintering temperatures (1550 °C and 1600 °C) were used for the 7YSZ and 8YSZ series. The series of sintered specimens were ground and polished to reach a good surface quality. Several mechanical tests of the materials were performed, namely, the microhardness test, fracture toughness test by the indentation method, and single-edge notch beam (SENB) test under three-point bending. Based on XRD analysis, the phase balance (percentages of tetragonal, cubic, and monoclinic ZrO₂ phases) of each composition was substantiated. The morphology of the fracture surfaces of specimens after both the fracture toughness tests was studied in relation to the mechanical behavior of the specimens and the microstructure of corresponding materials. SEM-EDX analysis was used for microstructural characterization. It was found that both the yttria percentage and sintering temperature affect the mechanical behavior of the ceramics. Optimal chemical composition and sintering temperature were determined for the studied series of ceramics. The maximum transformation toughening effect was revealed for ZrO₂-6 mol% Y₂O₃ ceramics during indentation. However, in the case of a SENB test, the maximum transformation toughening effect in the crack tip vicinity was found in ZrO₂-7 mol% Y₂O₃ ceramics. The conditions for obtaining YSZ ceramics with high fracture toughness are discussed.

Currently, ceramics are widely used in various industry branches, especially in energy, chemistry, and aerospace, as well as in medicine. Yttria-stabilized zirconia (YSZ) having unique electrical, thermal, and mechanical properties is one of the most popular ceramics for such applications. In this study, the influence of sintering temperature and yttria percentage on the microstructure and mechanical behavior of YSZ ceramics have been investigated. Corresponding mixtures of ZrO₂ powder doped with 3 and 6 mol% Y₂O₃ powders (hereinafter: 3YSZ and 6YSZ) were prepared, and a series of ceramic specimens were sintered in argon at 1450 °C, 1500 °C, and 1550 °C for 2 h. Changes in the morphology and size of microstructural components as well as their distribution were analyzed with respect to the sintering mode, phase composition, flexural strength, and fracture surface morphology. The 3YSZ and 6YSZ ceramics sintered for 2 h at 1550 °C and 1450 °C, respectively, exhibited the highest levels of strength due to the presence of agglomerates of fine tetragonal zirconia phase particles with high bond strength, as well as larger grains of the monoclinic zirconia phase. The dominant fracture micromechanisms in both the 3YSZ and 6YSZ ceramics related to their high strength are discussed.